PA612 77G33L NC010 DUPONT USA

Zytel®

Automotive Applications,Fitness equipment,electrical equipment

wear resistant,High impact resistance

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

thermal performance	Test Condition	Test Method	DUPONT USA/77G33L NC010
Combustibility (rate)		UL 94	HB
Glass transition temperature		ISO 11357-2	65.0 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	216 °C
		1.8MPa,Unannealed	ISO 75-2/A	200 °C
		HDT	ASTM D648/ISO 75	200 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.83-1.58
		MD：--	ISO 11359-2	2E-05 cm/cm/°C
		MD：55to160°C	ISO 11359-2	1.4E-05 cm/cm/°C
		TD：-40to23°C	ISO 11359-2	8.3E-05 cm/cm/°C
		MD：-40to23°C	ISO 11359-2	2.6E-05 cm/cm/°C
		TD：55to160°C	ISO 11359-2	1.6E-04 cm/cm/°C
		TD：--	ISO 11359-2	1.1E-04 cm/cm/°C
		TD：EffectiveThermalDiffusivity	ISO 11359-2	7.5E-08 m²/s
Melting temperature		ISO 11357-3	218 °C
Melting temperature				218 ℃（℉）

mechanical properties	Test Condition	Test Method	DUPONT USA/77G33L NC010
Bending modulus		ISO 178	8500 Mpa
Bending modulus			ASTM D790/ISO 178	8200 kg/cm²(MPa)[Lb/in²]
bending strength		ISO 178	260 Mpa
Charpy Notched Impact Strength		ASTM D256/ISO 179	60 kg·cm/cm(J/M)ft·lb/in
Compressive stress		ISO 604	160 Mpa
Elongation at Break		ASTM D412/ISO 527	3.2 %
shear strength		ASTM D732	75.0 Mpa
Tensile modulus		ISO 527-2	9500 Mpa
Tensile modulus			ASTM D412/ISO 527	9500 kg/cm²(MPa)[Lb/in²]
Tensile strain	Break	ISO 527-2	3.2 %
tensile strength		ASTM D412/ISO 527	168 kg/cm²(MPa)[Lb/in²]
tensile strength		Break	ISO 527-2	170 Mpa

Electrical performance	Test Condition	Test Method	DUPONT USA/77G33L NC010
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dielectric loss		ASTM D150/IEC 60250	4.1
Dielectric strength		IEC 60243-1	33 KV/mm
Dissipation factor	1MHz	IEC 60250	0.020
Dissipation factor		100Hz	IEC 60250	0.014
Relative permittivity	100Hz	IEC 60250	4.10
Relative permittivity		1MHz	IEC 60250	3.70
Surface resistivity		ASTM D257/IEC 60093	1.00E+12 Ω
Surface resistivity			IEC 60093	-- ohms
Volume resistivity		IEC 60093	1E+15 ohms·cm
Volume resistivity			ASTM D257/IEC 60093	1.00E+13 Ω.cm

other	Test Condition	Test Method	DUPONT USA/77G33L NC010
characteristic			PA612.33％玻纤增强.注塑成型

Physical properties	Test Condition	Test Method	DUPONT USA/77G33L NC010
density		ASTM D792/ISO 1183	1.32
Shrinkage rate		ASTM D955	0.3-0.9 %
		MD：3.20mm		0.20 %
		TD：3.20mm		1.0 %
		MD	ISO 294-4	0.30 %
		TD	ISO 294-4	0.90 %
SpecificHeatCapacity of Melt			2130 J/kg/°C
Stickiness		ISO 307	100 cm³/g
ThermalConductivityofMelt			0.26 W/m/K
Top out temperature			210 °C
Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.70 %
		23°C,24hr	ISO 62	0.30 %
		Saturation,23°C,2.00mm	ISO 62	1.8 %
			ASTM D570/ISO 62	0.7 %

impact performance	Test Condition	Test Method	DUPONT USA/77G33L NC010
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	80 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	70 kJ/m²
Suspended wall beam without notch impact strength		-30°C	ISO 180/1U	60 kJ/m²

flammability	Test Condition	Test Method	DUPONT USA/77G33L NC010
Burning rate	1.00mm	ISO 3795	23 mm/min
Extreme Oxygen Index		ISO 4589-2	23 %
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	1E-04 g
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
		0.70mm	UL 94	HB
		0.70mm	IEC 60695-11-10,-20	HB
		1.5mm	UL 94	HB