PA66 Leona™ FG172 ASAHI JAPAN
304
- Unit Price:US$ 4,639 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Thermal stability
- Application Areas:Electrical components｜switch｜Laptop case｜Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 95 |
| M级 | ISO 2039-2 | 95 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.82MPa,干 | ASTM D-648 | 248 °C |
| UL flame retardant rating | 干 | UL 94 | V-0 |
| Heat Deflection Temperature | 0.46MPa,干 | ASTM D-648 | 255 °C |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 3 ×10-5/K |
| Heat Deflection Temperature | 0.45MPa,未退火 | ASTM D648 | 255 °C |
| 0.45MPa,未退火 | ISO 75-2/B | 256 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 240 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 3E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ASTM D648 | 248 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ASTM D2863 | 37 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 湿 | 0.9 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | 干 | ASTM D-2863 | 37 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 64 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 干 | 旭化成方法 | 0.4-0.9 % |
| Wear factor | 湿 | ASTM D-1044 | 24 ×10-6kg/1000times |
| shrinkage rate | 吸水率(饱和,23°C) | 内部方法 | -- % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
| shrinkage rate | TD | 内部方法 | 0.90 % |
| MD | 内部方法 | 0.40 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1E+14 ohms | |
| IEC 60093 | 1E+14 ohms | ||
| volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| 23°C | IEC 60093 | 1E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 28 KV/mm | |
| IEC 60243-1 | 28 KV/mm | ||
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | 干(湿) | ASTM D-790 | 216(177) Mpa |
| tensile strength | 干(湿) | ASTM D-638 | 153(123) Mpa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 95(55) M Scale |
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 63(72) J/m |
| Elongation at break | 干(湿) | ASTM D-638 | 2.5(2.7) % |
| flexural coefficient | 干(湿) | ASTM D-790 | 7.6(5.9) GPa |
| bending strength | 23°C | ISO 178 | 208 Mpa |
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| Tensile modulus | 23°C | ISO 527-2 | 9100 Mpa |
| tensile strength | ASTM D638 | 153 Mpa | |
| 断裂,23°C | ISO 527-2 | 136 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.5 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
| flexural modulus | ASTM D790 | 7600 Mpa | |
| 23°C | ISO 178 | 8000 Mpa | |
| bending strength | ASTM D790 | 216 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.