Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 FG172 ASAHI JAPAN
Leona™
Electrical components,switch,Laptop case,Electronic field,Electrical field
Flame retardant,Thermal stability
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | ASAHI JAPAN/FG172 |
|---|---|---|---|
| Limiting Oxygen Index | 干 | ASTM D-2863 | 37 % |
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/FG172 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 64 kJ/m² |
| hardness | Test Condition | Test Method | ASAHI JAPAN/FG172 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 95 |
| M级 | ISO 2039-2 | 95 |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/FG172 |
|---|---|---|---|
| Water absorption rate | 湿 | 0.9 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/FG172 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 63(72) J/m |
| flexural coefficient | 干(湿) | ASTM D-790 | 7.6(5.9) GPa |
| bending strength | ASTM D790 | 216 Mpa | |
| tensile strength | 干(湿) | ASTM D-638 | 153(123) Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 9100 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 136 Mpa |
| Flexural modulus | ASTM D790 | 7600 Mpa | |
| tensile strength | ASTM D638 | 153 Mpa | |
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| Rockwell hardness | 干(湿) | ASTM D-785 | 95(55) M Scale |
| elongation | 断裂 | ASTM D638 | 2.5 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.5 % |
| bending strength | 23°C | ISO 178 | 208 Mpa |
| 干(湿) | ASTM D-790 | 216(177) Mpa | |
| Flexural modulus | 23°C | ISO 178 | 8000 Mpa |
| elongation at break | 干(湿) | ASTM D-638 | 2.5(2.7) % |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/FG172 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 2 |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 28 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+14 ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | ASTM D149 | 28 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+14 ohms |
| flammability | Test Condition | Test Method | ASAHI JAPAN/FG172 |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| Limiting Oxygen Index | ASTM D2863 | 37 % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/FG172 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.40 % |
| Wear factor | 湿 | ASTM D-1044 | 24 ×10-6kg/1000times |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
| Shrinkage rate | 吸水率(饱和,23°C) | 内部方法 | -- % |
| TD | 内部方法 | 0.90 % | |
| 干 | 旭化成方法 | 0.4-0.9 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/FG172 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 248 °C |
| 1.82MPa,干，HDT | ASTM D-648 | 248 °C | |
| 0.45MPa,未退火，HDT | ASTM D648 | 255 °C | |
| 0.46MPa,干，HDT | ASTM D-648 | 255 °C | |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 256 °C | |
| UL flame retardant rating | 干 | UL 94 | V-0 |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 240 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 3E-05 cm/cm/°C |
| 干 | ASTM D-696 | 3 ×10-5/K |