PC/ABS LUPOY® HR-5007A LG CHEM KOREA
304
- Unit Price:US$ 3,725 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:heat-resisting
- Application Areas:Electrical applications｜Automotive interior parts｜Electrical components｜Electrical/Electronic Applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 114 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,6.40mm,InjectionMolded | ASTM D648 | 113 °C |
| 1.8MPa | ISO 75-22 | 104 °C | |
| Glass Transition Temperature | ISO 11357-22 | 150 °C | |
| vicat | 50N | ISO 3062 | 119 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-22 | 7.7E-05 cm/cm/°C |
| TD | ISO 11359-22 | 8.3E-05 cm/cm/°C | |
| RTI Elec | 1.6mm | UL 746 | 60.0 °C |
| 3.0mm | UL 746 | 60.0 °C | |
| RTI Imp | 1.6mm | UL 746 | 60.0 °C |
| 3.0mm | UL 746 | 60.0 °C | |
| RTI Str | 1.6mm | UL 746 | 60.0 °C |
| 3.0mm | UL 746 | 60.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| 3.0mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA2 | NoBreak |
| -30°C | ISO 179/1eA2 | 36.3 kJ/m² | |
| 23°C | ISO 179/1eU2 | NoBreak | |
| -30°C | ISO 179/1eU2 | NoBreak | |
| Impact strength of cantilever beam gap | -30°C,3.20mm,注塑 | ASTM D256 | 490 J/m |
| 23°C,3.20mm,注塑 | ASTM D256 | 640 J/m | |
| ASTM D256 | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.14 g/cm³ | |
| ISO 11832 | 1130 kg/m3 | ||
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 5.3 g/10min |
| Melt volume flow rate | 260°C/5.0kg | ISO 11332 | 18.0 cm3/10min |
| shrinkage rate | MD：3.20mm,InjectionMolded | ASTM D955 | 0.50-0.80 % |
| Water absorption rate | 饱和 | ISO 622 | 0.15 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 600932 | 3.8E+14 ohms | |
| volume resistivity | IEC 600932 | >1.0E+13 ohms·m | |
| dielectric strength | IEC 60243-12 | 42 KV/mm | |
| relative permittivity | 1MHz | IEC 602502 | 2.80 |
| Dissipation Factor | 1MHz | IEC 602502 | 0.010 |
| arc resistance | ASTM D495 | PLC6 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| IEC 601122 | PLC 3 | ||
| High arc combustion index (HAI) | 1.6mm | UL 746 | PLC 1 |
| 3.0mm | UL 746 | PLC 1 | |
| High Voltage Arc Traceability Rate (HVTR) | PLC | UL 746 | |
| Hot wire ignition (HWI) | 1.6mm | UL 746 | PLC 3 |
| 3.0mm | UL 746 | PLC 3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | Break,3.20mm,InjectionMolded | ASTM D638 | >100 % |
| Nominal fracture strain | ISO 527-22 | >50 % | |
| flexural modulus | 3.20mm,InjectionMolded | ASTM D790 | 2110 Mpa |
| bending strength | 3.20mm | ASTM D790 | 77.5 Mpa |
| Tensile modulus | ISO 527-22 | 2200 Mpa | |
| tensile strength | 屈服,3.20mm,注塑 | ASTM D638 | 56.9 Mpa |
| 屈服 | ISO 527-22 | 60.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-22 | 4.9 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.