PC/ABS
PC/ABS LG CHEM KOREA HR-5007A
Injection grade
UL
US$ 3,240 / MT
FOB Guangzhou port, China
mechanical propertiesTest ConditionTest MethodLG CHEM KOREA/HR-5007A
Tensile strainBreak,3.20mm,InjectionMoldedASTM D638>100 %
tensile strengthYield,3.20mm,InjectionASTM D63856.9 Mpa
YieldISO 527-2260.0 Mpa
Bending modulus3.20mm,InjectionMoldedASTM D7902110 Mpa
Nominal fracture strainISO 527-22>50 %
Tensile strainYieldISO 527-224.9 %
Tensile modulusISO 527-222200 Mpa
bending strength3.20mmASTM D79077.5 Mpa
impact performanceTest ConditionTest MethodLG CHEM KOREA/HR-5007A
Charpy Notched Impact Strength-30°CISO 179/1eA236.3 kJ/m²
23°CISO 179/1eU2NoBreak
Impact strength of cantilever beam gap23°C,3.20mm,InjectionASTM D256640 J/m
-30°C,3.20mm,InjectionASTM D256490 J/m
Charpy Notched Impact Strength23°CISO 179/1eA2NoBreak
Impact strength of cantilever beam gapASTM D256NoBreak
Charpy Notched Impact Strength-30°CISO 179/1eU2NoBreak
Physical propertiesTest ConditionTest MethodLG CHEM KOREA/HR-5007A
densityISO 118321130 kg/m3
melt mass-flow rate250°C/2.16kgASTM D12385.3 g/10min
Water absorption rateSaturationISO 6220.15 %
densityASTM D7921.14 g/cm³
Shrinkage rateMD：3.20mm,InjectionMoldedASTM D9550.50-0.80 %
Melt Volume Flow Rate (MVR)260°C/5.0kgISO 1133218.0 cm3/10min
thermal performanceTest ConditionTest MethodLG CHEM KOREA/HR-5007A
Hot deformation temperature1.8MPaISO 75-22104 °C
RTI Imp3.0mmUL 74660.0 °C
RTI Str1.6mmUL 74660.0 °C
Glass transition temperatureISO 11357-22150 °C
Vicat softening temperature50NISO 3062119 °C
RTI Imp1.6mmUL 74660.0 °C
Linear coefficient of thermal expansionTDISO 11359-228.3E-05 cm/cm/°C
RTI Elec3.0mmUL 74660.0 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mm,InjectionMoldedASTM D648113 °C
Linear coefficient of thermal expansionMDISO 11359-227.7E-05 cm/cm/°C
RTI Elec1.6mmUL 74660.0 °C
RTI Str3.0mmUL 74660.0 °C
Electrical performanceTest ConditionTest MethodLG CHEM KOREA/HR-5007A
High arc combustion index1.6mmUL 746PLC 1
Dissipation factor1MHzIEC 6025020.010
Dielectric strengthIEC 60243-1242 KV/mm
Hot wire ignition3.0mmUL 746PLC 3
Compared to the anti leakage trace indexCTIUL 746PLC 0
Relative permittivity1MHzIEC 6025022.80
Arc resistanceASTM D495PLC6
Surface resistivityIEC 6009323.8E+14 ohms
High arc combustion index3.0mmUL 746PLC 1
Hot wire ignition1.6mmUL 746PLC 3
Volume resistivityIEC 600932>1.0E+13 ohms·m
Compared to the anti leakage trace indexIEC 601122PLC 3
flammabilityTest ConditionTest MethodLG CHEM KOREA/HR-5007A
UL flame retardant rating3.0mmUL 94HB
1.6mmUL 94HB
hardnessTest ConditionTest MethodLG CHEM KOREA/HR-5007A
Rockwell hardnessR-ScaleASTM D785114

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China