LCP SUMIKASUPER® E6810KHF B Z SUMITOMO JAPAN
221
- Unit Price:US$ 6,194 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:32MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Dimensional stability｜Low warpage｜Low viscosity｜High elasticity｜High temperature strength｜Aging resistance
- Application Areas:Electrical appliances｜Engineering accessories｜Automotive sector｜Food containers｜Electronic field｜Electrical field
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 103 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ASTM D648 | 284 °C |
| Linear coefficient of thermal expansion | 流动 : 50 到 150°C | ASTM D696 | 1.1E-5 cm/cm/°C |
| 横向 : 50 到 150°C | ASTM D696 | 6.5E-5 cm/cm/°C | |
| RTI Elec | 3.2 mm | UL 746 | 220 °C |
| RTI Imp | 3.2 mm | UL 746 | 200 °C |
| RTI | 3.2 mm | UL 746 | 240 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.30 mm | UL 94 | V-0 |
| Limiting Oxygen Index | ASTM D2863 | 46 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 6.40 mm | ASTM D256 | 280 J/m |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | 流动 | ASTM D955 | 0.22 % |
| 横向流动 | ASTM D955 | 0.66 % | |
| Water absorption rate | 饱和 | ASTM D570 | 0.020 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| dielectric constant | 1 kHz | ASTM D150 | 4.30 |
| 1 MHz | ASTM D150 | 3.90 | |
| Dissipation Factor | 1 kHz | ASTM D150 | 0.019 |
| 1 MHz | ASTM D150 | 0.028 | |
| arc resistance | ASTM D495 | 130 sec | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | V |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 to 150 °C | ||
| drying time | 3.0 hr | ||
| Suggested maximum material return ratio | 30 % | ||
| Temperature at the rear of the barrel | 300 to 320 °C | ||
| Temperature in the middle of the barrel | 320 to 350 °C | ||
| Temperature at the front of the material cylinder | 340 to 370 °C | ||
| Spray nozzle temperature | 340 to 370 °C | ||
| mold temperature | 70 to 160 °C | ||
| Injection Pressure | 78.0 to 157 Mpa | ||
| injection speed | 中等偏快 | ||
| pressure holding | 20.0 to 39.0 Mpa | ||
| Back pressure | 0.980 to 4.90 Mpa | ||
| screw speed | 50 to 100 rpm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 126 Mpa | |
| elongation | 断裂 | ASTM D638 | 4.3 % |
| flexural modulus | 23°C | ASTM D790 | 13500 Mpa |
| bending strength | 23°C | ASTM D790 | 134 Mpa |
| shear strength | ASTM D732 | 50.0 Mpa | |
| Poisson's ratio | ASTM E132 | 0.39 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.