LCP E6810KHF B Z SUMITOMO JAPAN
SUMIKASUPER®
Electrical appliances、Engineering accessories、Automotive sector、Food containers、Electronic field、Electrical field
Dimensional stability、Low warpage、Low viscosity、High elasticity、High temperature strength、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SUMITOMO JAPAN/E6810KHF B Z |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 6.40 mm | ASTM D256 | 280 J/m |
| hardness | Test Condition | Test Method | SUMITOMO JAPAN/E6810KHF B Z |
|---|---|---|---|
| Rockwell hardness | R 级 | ASTM D785 | 103 |
| Mechanical properties | Test Condition | Test Method | SUMITOMO JAPAN/E6810KHF B Z |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 4.3 % |
| bending strength | 23°C | ASTM D790 | 134 Mpa |
| shear strength | ASTM D732 | 50.0 Mpa | |
| Poisson's ratio | ASTM E132 | 0.39 | |
| Flexural modulus | 23°C | ASTM D790 | 13500 Mpa |
| tensile strength | ASTM D638 | 126 Mpa |
| Electrical performance | Test Condition | Test Method | SUMITOMO JAPAN/E6810KHF B Z |
|---|---|---|---|
| Dissipation Factor | 1 kHz | ASTM D150 | 0.019 |
| Volume resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | V | |
| dielectric constant | 1 MHz | ASTM D150 | 3.90 |
| 1 kHz | ASTM D150 | 4.30 | |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.028 |
| arc resistance | ASTM D495 | 130 sec |
| flammability | Test Condition | Test Method | SUMITOMO JAPAN/E6810KHF B Z |
|---|---|---|---|
| UL flame retardant rating | 0.30 mm | UL 94 | V-0 |
| Limiting Oxygen Index | ASTM D2863 | 46 % |
| physical property | Test Condition | Test Method | SUMITOMO JAPAN/E6810KHF B Z |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D570 | 0.020 % |
| Shrinkage rate | 流动 | ASTM D955 | 0.22 % |
| 横向流动 | ASTM D955 | 0.66 % |
| Thermal performance | Test Condition | Test Method | SUMITOMO JAPAN/E6810KHF B Z |
|---|---|---|---|
| Linear coefficient of thermal expansion | 横向 : 50 到 150°C | ASTM D696 | 6.5E-5 cm/cm/°C |
| RTI | 3.2 mm | UL 746 | 240 °C |
| RTI Elec | 3.2 mm | UL 746 | 220 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 284 °C |
| Linear coefficient of thermal expansion | 流动 : 50 到 150°C | ASTM D696 | 1.1E-5 cm/cm/°C |
| RTI Imp | 3.2 mm | UL 746 | 200 °C |
| injection | Test Condition | Test Method | SUMITOMO JAPAN/E6810KHF B Z |
|---|---|---|---|
| screw speed | 50 to 100 rpm | ||
| Suggested maximum material return ratio | 30 % | ||
| Injection Pressure | 78.0 to 157 Mpa | ||
| drying temperature | 120 to 150 °C | ||
| drying time | 3.0 hr | ||
| pressure holding | 20.0 to 39.0 Mpa | ||
| Temperature in the middle of the barrel | 320 to 350 °C | ||
| Temperature at the rear of the barrel | 300 to 320 °C | ||
| Temperature at the front of the material cylinder | 340 to 370 °C | ||
| Back pressure | 0.980 to 4.90 Mpa | ||
| Temperature | 70 to 160 °C | ||
| injection speed | 中等偏快 | ||
| Spray nozzle temperature | 340 to 370 °C |