PC/PBT VALOX™ 420SE0-1001 SABIC INNOVATIVE NANSHA

380

Unit Price:US$ 4,480 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
73MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:Trimming machine｜Food mixer motor stator and commutator｜Electric fan｜Laptop case｜Spool｜Switches｜ etc
Color:--
Grade:Injection grade

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	洛氏硬度 R	ASTM D 785	119	-
Bending modulus	挠曲模量，1.3 mm/min, 50 mm span	ASTM D 790	9400	Mpa
Tensile stress	拉伸伸长,Yield,类型L, 5 mm/min	ASTM D 638	1.2	%
	Tensile stress	抗张程度，Break，类型L, 5 mm/min，Yield	ASTM D 638	95	Mpa
	Tensile stress	Tensile stress	抗张程度，Yield，类型L，5 mm/min	ASTM D 638	95	Mpa
Flexural Stress, brk	弯曲强度，Break,1.3 mm/min, 50 mm span	ASTM D 790	186	Mpa
Tensile modulus	拉伸模量,5 mm/min	ASTM D 638	11500	Mpa
Tensile stress	拉伸伸长,Break，类型L, 5 mm/min，Yield	ASTM D 638	1.2	%
Tensile strength	Yield，类型L，5 mm/min	ASTM D 638	95	Mpa
Tensile strength	Tensile strength	Break，类型L, 5 mm/min	ASTM D 638	95	Mpa
elongation	Yield,类型L, 5 mm/min	ASTM D 638	1.2	%
Bending modulus	1.3 mm/min, 50 mm span	ASTM D 790	9400	Mpa
bending strength	Break,1.3 mm/min, 50 mm span	ASTM D 790	186	Mpa
Rockwell hardness	R	ASTM D 785	119	-
Tensile modulus	5 mm/min	ASTM D 638	11500	Mpa
elongation	Break，类型L, 5 mm/min	ASTM D 638	1.2	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Relative Temp Index. Elec	相对热指数，电性能	UL 746B	130	°C
Linear coefficient of thermal expansion	60℃ to 138℃, flow （Flow）	ASTM E 831	0.0000252	1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	-40℃ to 4O℃,flow （Flow）	ASTM E 831	0.0000252	1/℃
Hot deformation temperature	1.82 MPa, 6.4 mm, unannealed （Unannealed）	ASTM D 648	204	°C
	Hot deformation temperature	0.45 MPa, 6.4 mm， unannealed （Unannealed）	ASTM D 648	215	°C
		Hot deformation temperature	1.82 MPa, 3.2mm, unannealed （Unannealed）	ASTM D 648	200	°C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, 3.2 mm, unannealed （未 Annealed）	ASTM D 648	212	°C
Vicat softening temperature	维卡软化温度，等级 B/50	ASTM D 1525	200	°C
Relative Temp Index, Meeh w/impact	相对热指数，机械冲击性能	UL 746B	130	°C
Relative Temp Index, Meeh w/o impact	相对热指数，非机械冲击性能	UL 746B	140	°C
Hot deformation temperature	1.82 MPa, 3.2mm, Unannealed	ASTM D 648	200	°C
	Hot deformation temperature	0.45 MPa, 6.4 mm，Unannealed	ASTM D 648	215	°C
	Hot deformation temperature	Hot deformation temperature	1.82 MPa, 6.4 mm, Unannealed	ASTM D 648	204	°C
Linear coefficient of thermal expansion	-40℃-4O℃, Flow	ASTM E 831	0.0000252	1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	60℃-138℃, Flow	ASTM E 831	0.0000252	1/℃
Hot deformation temperature	0.45 MPa, 3.2 mm, Unannealed	ASTM D 648	212	°C
Physical property type	Test Condition	Test Method	Test Result	Test Unit
Test project	测试条件	测试方法	测试结果	测试单位
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	xflow （Across Flow），3.2-4.6mm	SABIC method	0.6-1	%
	Shrinkage rate	xflow （Across Flow）,1.5-3.2 mm	SABIC method	0.4 - 0.6	%
		Shrinkage rate	flow （Flow），3.2-4.6 mm	SABIC method	0.5 - 0.8	%
			Shrinkage rate	flow （Flow）,1.5-3.2 mm	SABIC method	0.3 - 0.5	%
			Shrinkage rate	Shrinkage rate	flow （Flow），3.2 mm	SABIC method	0.5 - 0.7	%
Water absorption rate	24 hours	ASTM D 570	0.06	%
Specific Volume		ASTM D 792	0.62	cm³/g
density	比重	ASTM D 792	1.61	—
Bi Rong		ASTM D 792	0.62	cm³/g
density		ASTM D 792	1.61	—
Shrinkage rate	Across Flow，3.2-4.6mm	SABIC method	0.6-1	%
	Shrinkage rate	Flow, 1.5-3.2 mm	SABIC method	0.3 - 0.5	%
		Shrinkage rate	Flow，3.2-4.6 mm	SABIC method	0.5 - 0.8	%
			Shrinkage rate	Across Flow ,1.5-3.2 mm	SABIC method	0.4 - 0.6	%
			Shrinkage rate	Shrinkage rate	Flow，3.2 mm	SABIC method	0.5 - 0.7	%
Water absorption rate	24 hours	ASTM D 570	0.06	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan East Asia	US$ 4480 /MT
Guangzhou HuShang Chemical	US$ 4940 /MT
Dongguan Guangyan	US$ 4940 /MT

Supplier Join

Get App

Top

PC/PBT VALOX™ 420SE0-1001 SABIC INNOVATIVE NANSHA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index