Mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420SE0-1001
Flexural Stress, brk	弯曲强度，断裂,1.3 mm/min, 50 mm span	ASTM D 790	186 Mpa
Tensile stress	拉伸伸长,屈服,类型L, 5 mm/min	ASTM D 638	1.2 %
Tensile stress		拉伸伸长,断裂，类型L, 5 mm/min，屈服	ASTM D 638	1.2 %
Tensile modulus	拉伸模量,5 mm/min	ASTM D 638	11500 Mpa
Rockwell hardness	洛氏硬度 R	ASTM D 785	119 -
bending strength	断裂,1.3 mm/min, 50 mm span	ASTM D 790	186 Mpa
Flexural modulus	挠曲模量，1.3 mm/min, 50 mm span	ASTM D 790	9400 Mpa
Rockwell hardness	R	ASTM D 785	119 -
Tensile strength	屈服，类型L，5 mm/min	ASTM D 638	95 Mpa
elongation	屈服,类型L, 5 mm/min	ASTM D 638	1.2 %
Tensile stress	抗张程度，断裂，类型L, 5 mm/min，屈服	ASTM D 638	95 Mpa
Tensile stress		抗张程度，屈服，类型L，5 mm/min	ASTM D 638	95 Mpa
Flexural modulus	1.3 mm/min, 50 mm span	ASTM D 790	9400 Mpa
Tensile strength	断裂，类型L, 5 mm/min	ASTM D 638	95 Mpa
elongation	断裂，类型L, 5 mm/min	ASTM D 638	1.2 %
Tensile modulus	5 mm/min	ASTM D 638	11500 Mpa

physical property	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420SE0-1001
Specific Volume		ASTM D 792	0.62 cm³/g
density	比重	ASTM D 792	1.61 —
specific volume		ASTM D 792	0.62 cm³/g
Water absorption rate	24 hours	ASTM D 570	0.06 %
Shrinkage rate	xflow （横向），3.2-4.6mm	SABIC method	0.6-1 %
density		ASTM D 792	1.61 —
Shrinkage rate	xflow （横向）,1.5-3.2 mm	SABIC method	0.4 - 0.6 %
		流动，3.2-4.6 mm	SABIC method	0.5 - 0.8 %
		flow （流动），3.2 mm	SABIC method	0.5 - 0.7 %
		横向 ,1.5-3.2 mm	SABIC method	0.4 - 0.6 %
		流动，3.2 mm	SABIC method	0.5 - 0.7 %
		横向，3.2-4.6mm	SABIC method	0.6-1 %
		flow （流动）,1.5-3.2 mm	SABIC method	0.3 - 0.5 %
		flow （流动），3.2-4.6 mm	SABIC method	0.5 - 0.8 %
		流动, 1.5-3.2 mm	SABIC method	0.3 - 0.5 %

Thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420SE0-1001
Linear coefficient of thermal expansion	60℃-138℃, 流动	ASTM E 831	0.0000252 1/℃
Heat distortion temperature	0.45 MPa, 6.4 mm， unannealed （未退火），HDT	ASTM D 648	215 °C
		1.82 MPa, 6.4 mm, unannealed （未退火），HDT	ASTM D 648	204 °C
		0.45 MPa, 3.2 mm, 未退火，HDT	ASTM D 648	212 °C
		1.82 MPa, 3.2mm, 未退火，HDT	ASTM D 648	200 °C
		0.45 MPa, 3.2 mm, unannealed （未退火），HDT	ASTM D 648	212 °C
Linear coefficient of thermal expansion	60℃ to 138℃, flow （流动）	ASTM E 831	0.0000252 1/℃
Relative Temp Index, Meeh w/impact	相对热指数，机械冲击性能	UL 746B	130 °C
Linear coefficient of thermal expansion	-40℃ to 4O℃,flow （流动）	ASTM E 831	0.0000252 1/℃
vicat	维卡软化温度，等级 B/50	ASTM D 1525	200 °C
Relative Temp Index. Elec	相对热指数，电性能	UL 746B	130 °C
Heat distortion temperature	1.82 MPa, 6.4 mm, 未退火，HDT	ASTM D 648	204 °C
		0.45 MPa, 6.4 mm，未退火，HDT	ASTM D 648	215 °C
		1.82 MPa, 3.2mm, unannealed （未退火），HDT	ASTM D 648	200 °C
Relative Temp Index, Meeh w/o impact	相对热指数，非机械冲击性能	UL 746B	140 °C
Linear coefficient of thermal expansion	-40℃-4O℃, 流动	ASTM E 831	0.0000252 1/℃