PC INFINO® CF-3200HF Samsung Cheil South Korea

239

Unit Price:US$ 3,477 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜Flame retardant
Application Areas:Phone｜Electronic and Electrical Applications
Color:--
Grade:--

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C6	ISO 180/1A	19 kJ/m²
	Impact strength of cantilever beam gap	23°C, 6.35 mm	ASTM D256	200 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C, 3.18 mm	ASTM D256	190 J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	25 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8 mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	3.2 mm	UL 94	V-1

mechanical properties	Test Condition	Test Method	Test Result
bending strength	--5	ISO 178	170 Mpa
bending strength	bending strength	--4	ASTM D790	140 Mpa
Bending modulus	--5	ISO 178	6000 Mpa
Bending modulus	Bending modulus	--4	ASTM D790	5500 Mpa
elongation	Break	ISO 527-2/5	4.3 %
elongation	elongation	Break3	ASTM D638	4.3 %
tensile strength	Break	ISO 527-2/5	200 Mpa
	tensile strength	Break3	ASTM D638	98.0 Mpa
		tensile strength	Yield	ISO 527-2/5	100 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	98.0 Mpa
Tensile modulus	--	ISO 527-2/5	5700 Mpa
Tensile modulus	Tensile modulus	--3	ASTM D638	5300 Mpa

injection	Test Condition	Test Method	Test Result
Hot air dryer			100 °C
Vacuum drying machine			100 °C
Hot air dryer			2.0 to 4.0 hr
Vacuum drying machine			4.0 to 6.0 hr
Suggested maximum moisture content			0.10 %
Temperature at the rear of the barrel			270 °C
Temperature in the middle of the barrel			280 to 290 °C
Temperature at the front of the material cylinder			300 °C
Spray nozzle temperature			300 °C
Mold temperature			80 to 120 °C
Injection pressure			98.1 Mpa
Back pressure			0.981 to 2.94 Mpa
Screw speed			40 to 80 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	145 °C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	144 °C
		Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	141 °C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	139 °C
Vicat softening temperature		ISO 306/B50	148 °C

Physical properties	Test Condition	Test Method	Test Result
density	本色	ASTM D792	1.33 g/cm³
Water absorption rate	Saturation, 23°C	ASTM D570	0.15 %
Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.20 - 0.50 %
	Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.20 - 0.50 %
		Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.20 - 0.50 %
		Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.20 - 0.50 %
melt mass-flow rate	250°C/10.0 kg	ASTM D1238	23 g/10 min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R -Sale	ISO 2039-2	116
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	116

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.