Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC CF-3200HF Samsung Cheil South Korea
INFINO®
Phone、Electronic and Electrical
Glass fiber reinforced、Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/CF-3200HF |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 25 kJ/m² |
| Impact strength of cantilever beam gap | 23°C, 3.18 mm | ASTM D256 | 190 J/m |
| 23°C6 | ISO 180/1A | 19 kJ/m² | |
| 23°C, 6.35 mm | ASTM D256 | 200 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/CF-3200HF |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 116 |
| R 级 | ASTM D785 | 116 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/CF-3200HF |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 100 Mpa |
| 断裂 | ISO 527-2/5 | 200 Mpa | |
| 屈服3 | ASTM D638 | 98.0 Mpa | |
| elongation | 断裂3 | ASTM D638 | 4.3 % |
| bending strength | --4 | ASTM D790 | 140 Mpa |
| --5 | ISO 178 | 170 Mpa | |
| Tensile modulus | --3 | ASTM D638 | 5300 Mpa |
| Flexural modulus | --4 | ASTM D790 | 5500 Mpa |
| --5 | ISO 178 | 6000 Mpa | |
| tensile strength | 断裂3 | ASTM D638 | 98.0 Mpa |
| Tensile modulus | -- | ISO 527-2/5 | 5700 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 4.3 % |
| flammability | Test Condition | Test Method | Samsung Cheil South Korea/CF-3200HF |
|---|---|---|---|
| UL flame retardant rating | 3.2 mm | UL 94 | V-1 |
| 0.8 mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/CF-3200HF |
|---|---|---|---|
| density | 本色 | ASTM D792 | 1.33 g/cm³ |
| Shrinkage rate | 横向流动 : 3.20 mm | ASTM D955 | 0.20 - 0.50 % |
| 流量 : 2.00 mm | ISO 294-4 | 0.20 - 0.50 % | |
| 流动 : 3.20 mm | ASTM D955 | 0.20 - 0.50 % | |
| 横向流量 : 2.00 mm | ISO 294-4 | 0.20 - 0.50 % | |
| Water absorption rate | 饱和, 23°C | ASTM D570 | 0.15 % |
| melt mass-flow rate | 250°C/10.0 kg | ASTM D1238 | 23 g/10 min |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/CF-3200HF |
|---|---|---|---|
| vicat | ISO 306/B50 | 148 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm，HDT | ISO 75-2/A | 139 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 141 °C | |
| 0.45 MPa, 未退火, 4.00 mm，HDT | ISO 75-2/B | 144 °C | |
| 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 145 °C |
| injection | Test Condition | Test Method | Samsung Cheil South Korea/CF-3200HF |
|---|---|---|---|
| screw speed | 40 to 80 rpm | ||
| Suggested maximum moisture content | 0.10 % | ||
| Vacuum dryer | 100 °C | ||
| Injection Pressure | 98.1 Mpa | ||
| Hot air dryer | 2.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 280 to 290 °C | ||
| Temperature at the rear of the barrel | 270 °C | ||
| Vacuum dryer | 4.0 to 6.0 hr | ||
| Temperature at the front of the material cylinder | 300 °C | ||
| Back pressure | 0.981 to 2.94 Mpa | ||
| Temperature | 80 to 120 °C | ||
| Hot air dryer | 100 °C | ||
| Spray nozzle temperature | 300 °C |