PA66

PA66 Leona™ 90G60 ASAHI JAPAN

225

Unit Price:US$ 3,650 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
61.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High rigidity
Application Areas:Automotive External Parts
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	56 kJ/m²

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	湿		0.9 %

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus	23°C	ISO 178	15800 Mpa
Bending modulus	Bending modulus		ASTM D790	16000 Mpa
Tensile strain	Break,23°C	ISO 527-2	2.0 %
elongation	Break	ASTM D638	2.0 %
tensile strength	Break,23°C	ISO 527-2	189 Mpa
tensile strength	tensile strength		ASTM D638	190 Mpa
Tensile modulus	23°C	ISO 527-2	18200 Mpa
bending strength	23°C	ISO 178	324 Mpa
bending strength	bending strength		ASTM D790	300 Mpa
Rockwell hardness	干(湿)	ASTM D-785	95(88) M Scale
flexural coefficient	干(湿)	ASTM D-790	16.0(12.9) GPa
tensile strength	干(湿)	ASTM D-638	190(148) Mpa
Elongation at Break	干(湿)	ASTM D-638	2(3) %
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	95(100) J/m
bending strength	干(湿)	ASTM D-790	300(234) Mpa
Rockwell hardness	干(湿)	ASTM D-785	120(117) R scale

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity			0.30 W/m/K
specific heat			1840 J/kg/°C
Linear coefficient of thermal expansion	MD	ASTM D696	2E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	210 °C
Hot deformation temperature	Hot deformation temperature	1.82MPa,干	ASTM D-648	225 °C
specific heat	干		1840 J/(kg.k)
Linear coefficient of thermal expansion	干	ASTM D-696	2
thermal conductivity	干		0.3 W/(m.K)
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	230 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	225 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	-- %
Shrinkage rate	吸水率(Saturation,23°C)	Internal Method	-- %
	Shrinkage rate	MD	Internal Method	0.20 %
		Shrinkage rate	TD	Internal Method	0.50 %
		Shrinkage rate	Shrinkage rate	干	旭化成方法	0.2/0.5 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	3.00mm	IEC 60112	PLC 1
Dielectric strength		IEC 60243-1	28 KV/mm
Dielectric strength	Dielectric strength		ASTM D149	28 KV/mm
Surface resistivity		IEC 60093	1E+13 ohms
Surface resistivity	Surface resistivity		ASTM D257	1E+13 ohms

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale	ASTM D785	120
	Rockwell hardness	M-Sale	ISO 2039-2	95
		Rockwell hardness	R-Sale	ISO 2039-2	120
		Rockwell hardness	Rockwell hardness	M-Sale	ASTM D785	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.