Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 90G60 ASAHI JAPAN
Leona™
Automotive External Parts
High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/90G60 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 56 kJ/m² |
| hardness | Test Condition | Test Method | ASAHI JAPAN/90G60 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 95 |
| R计秤 | ISO 2039-2 | 120 | |
| M计秤 | ISO 2039-2 | 95 | |
| R计秤 | ASTM D785 | 120 |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/90G60 |
|---|---|---|---|
| Water absorption rate | 湿 | 0.9 % |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/90G60 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 1 |
| dielectric strength | IEC 60243-1 | 28 KV/mm | |
| Surface Resistivity | ASTM D257 | 1E+13 ohms | |
| dielectric strength | ASTM D149 | 28 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/90G60 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 95(100) J/m |
| bending strength | ASTM D790 | 300 Mpa | |
| flexural coefficient | 干(湿) | ASTM D-790 | 16.0(12.9) GPa |
| Tensile modulus | 23°C | ISO 527-2 | 18200 Mpa |
| tensile strength | 干(湿) | ASTM D-638 | 190(148) Mpa |
| 断裂,23°C | ISO 527-2 | 189 Mpa | |
| Flexural modulus | ASTM D790 | 16000 Mpa | |
| tensile strength | ASTM D638 | 190 Mpa | |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(117) R scale |
| elongation | 断裂 | ASTM D638 | 2.0 % |
| Rockwell hardness | 干(湿) | ASTM D-785 | 95(88) M Scale |
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.0 % |
| bending strength | 23°C | ISO 178 | 324 Mpa |
| 干(湿) | ASTM D-790 | 300(234) Mpa | |
| Flexural modulus | 23°C | ISO 178 | 15800 Mpa |
| elongation at break | 干(湿) | ASTM D-638 | 2(3) % |
| physical property | Test Condition | Test Method | ASAHI JAPAN/90G60 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.20 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
| Shrinkage rate | 吸水率(饱和,23°C) | 内部方法 | -- % |
| TD | 内部方法 | 0.50 % | |
| 干 | 旭化成方法 | 0.2/0.5 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/90G60 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 225 °C |
| specific heat | 干 | 1840 J/(kg.k) | |
| Heat distortion temperature | 1.82MPa,干，HDT | ASTM D-648 | 225 °C |
| thermal conductivity | 0.30 W/m/K | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 230 °C |
| thermal conductivity | 干 | 0.3 W/(m.K) | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 210 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 2E-05 cm/cm/°C |
| specific heat | 1840 J/kg/°C | ||
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 2 |
Contact Us
Get App
Top