TPEE

TPEE BEXLOY® 6356 DUPONT TAIWAN

339

Unit Price:US$ 6,690 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
93MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability
Application Areas:Pipeline components｜sheet｜Electric wire｜Cable Applications｜Industrial applications｜Automotive sector｜Filamentous｜Fitness equipment｜Electrical appliances
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 8256/1	300 kJ/m²
Charpy Notched Impact Strength	-40°C	ISO 179/1eA	15 kJ/m²
	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	25 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,Partial Break	ISO 179/1eA	120 kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	19 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	81 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	3.0mm	UL 94	HB
		UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	21 %
FMVSS flammability		FMVSS302	SE
Fogging-G-value	condensate	ISO 6452	1E-04 g

elastomer	Test Condition	Test Method	Test Result
tear strength	横向Flow	ISO 34-1	150 kN/m
tear strength	tear strength	Flow	ISO 34-1	160 kN/m

mechanical properties	Test Condition	Test Method	Test Result
Tensile creep modulus	1000hr	ISO 899-1	182 Mpa
Tensile creep modulus	Tensile creep modulus	1hr	ISO 899-1	248 Mpa
Nominal tensile fracture strain		ISO 527-2	500 %
Tensile strain	Break	ISO 527-2	>300 %
Tensile strain	Tensile strain	Yield	ISO 527-2	31 %
tensile strength	100%Strain	ISO 527-2	19.0 Mpa
	tensile strength	50%Strain	ISO 527-2	18.8 Mpa
		tensile strength	10%Strain	ISO 527-2	15.0 Mpa
			tensile strength	5.0%Strain	ISO 527-2	12.0 Mpa
			tensile strength	tensile strength	Break	ISO 527-2	43.0 Mpa
Tensile modulus		ISO 527-2	280 Mpa
tensile strength	Yield	ISO 527-2	20.0 Mpa
Bending modulus		ISO 178	290 Mpa
Wear resistance		ISO 4649	110 mm³

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	1.5E-04 cm/cm/°C
	Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	5.44E-08 m²/s
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	1.8E-04 cm/cm/°C
			Linear coefficient of thermal expansion	TD：23to55°C	ASTME831	1.7E-04 cm/cm/°C
				Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	1.6E-04 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：--	ISO 11359-2	1.9E-04 cm/cm/°C
Melting temperature		ISO 11357-3	210 °C
Vicat softening temperature	--	ISO 306/B50	100 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	195 °C
Glass transition temperature		ISO 11357-2	0.00 °C
Brittle temperature		ISO 974	-96.0 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	45.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	80.0 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.22 g/cm³
melt mass-flow rate	230°C/2.16kg	ISO 1133	9.0 g/10min
Melt Volume Flow Rate (MVR)	230°C/2.16kg	ISO 1133	8.50 cm3/10min
Water absorption rate	23°C,24hr	ISO 62	0.50 %
	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.60 %
	Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %
MediumDensity			1.06 g/cm³
SpecificHeatCapacity of Melt			2150 J/kg/°C
ThermalConductivityofMelt			0.15 W/m/K
Shrinkage rate	TD	ISO 294-4	1.5 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.5 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	100Hz	IEC 60250	0.012
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.036
Relative permittivity	1MHz	IEC 60250	4.10
Volume resistivity		IEC 60093	8E+13 ohms·cm
Surface resistivity		IEC 60093	>1.0E+15 ohms
Dielectric strength		IEC 60243-1	20 KV/mm
Relative permittivity	100Hz	IEC 60250	4.60

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD,15Sec	ISO 868	57
Shore hardness	Shore hardness	ShoreD	ISO 868	63

Supplementary Information	Test Condition	Test Method	Test Result
EmissionofOrganicCompounds		VDA277	2.50 µgC/g
Odor		VDA270	2.50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

TPEE BEXLOY® 6356 DUPONT TAIWAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet