Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPEE 6356 DUPONT TAIWAN
BEXLOY®
Pipeline components、sheet、Electric wire、Cable Applications、Industrial applications、Automotive sector、Filamentous、Fitness equipment、Electrical appliances
Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT TAIWAN/6356 |
|---|---|---|---|
| Tensile impact strength | 23°C | ISO8256/1 | 300 kJ/m² |
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 15 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 81 kJ/m² |
| Charpy Notched Impact Strength | 23°C,局部断裂 | ISO179/1eA | 120 kJ/m² |
| -30°C | ISO179/1eA | 25 kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 19 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT TAIWAN/6356 |
|---|---|---|---|
| 邵氏D,15秒 | ISO868 | 57 | |
| 邵氏D | ISO868 | 63 |
| Supplementary Information | Test Condition | Test Method | DUPONT TAIWAN/6356 |
|---|---|---|---|
| Emissions of Organic Compounds | VDA277 | 2.50 µgC/g | |
| Odor | VDA270 | 2.50 |
| Mechanical properties | Test Condition | Test Method | DUPONT TAIWAN/6356 |
|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 248 Mpa |
| Tensile stress | 屈服 | ISO527-2 | 20.0 Mpa |
| 50%应变 | ISO527-2 | 18.8 Mpa | |
| Tensile modulus | ISO527-2 | 280 Mpa | |
| Tensile stress | 5.0%应变 | ISO527-2 | 12.0 Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 182 Mpa |
| Tensile strain | 断裂 | ISO527-2 | >300 % |
| Nominal tensile fracture strain | ISO527-2 | 500 % | |
| Tensile stress | 断裂 | ISO527-2 | 43.0 Mpa |
| 10%应变 | ISO527-2 | 15.0 Mpa | |
| Tensile strain | 屈服 | ISO527-2 | 31 % |
| Flexural modulus | ISO178 | 290 Mpa | |
| Tensile stress | 100%应变 | ISO527-2 | 19.0 Mpa |
| abrasion resistance | ISO4649 | 110 mm³ |
| Electrical performance | Test Condition | Test Method | DUPONT TAIWAN/6356 |
|---|---|---|---|
| Dissipation Factor | 1MHz | IEC60250 | 0.036 |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| 1MHz | IEC60250 | 4.10 | |
| Volume resistivity | IEC60093 | 8E+13 ohms·cm | |
| dielectric strength | IEC60243-1 | 20 KV/mm | |
| Dissipation Factor | 100Hz | IEC60250 | 0.012 |
| 100Hz | IEC60250 | 4.60 |
| flammability | Test Condition | Test Method | DUPONT TAIWAN/6356 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| 3.0mm | UL94 | HB | |
| FMVSS flammability | FMVSS302 | SE | |
| UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | HB |
| 1.5mm | IEC60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO4589-2 | 21 % | |
| Fogging-G-value | condensate | ISO6452 | 1E-04 g |
| physical property | Test Condition | Test Method | DUPONT TAIWAN/6356 |
|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 1.5 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO62 | 0.60 % |
| Melt volume flow rate | 230°C/2.16kg | ISO1133 | 8.50 cm3/10min |
| MediumDensity | 1.06 g/cm³ | ||
| melt mass-flow rate | 230°C/2.16kg | ISO1133 | 9.0 g/10min |
| Shrinkage rate | MD | ISO294-4 | 1.5 % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.50 % |
| density | ISO1183 | 1.22 g/cm³ | |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 % |
| SpecificHeatCapacity of Melt | 2150 J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 W/m/K |
| elastomer | Test Condition | Test Method | DUPONT TAIWAN/6356 |
|---|---|---|---|
| tear strength | 横向流量 | ISO34-1 | 150 kN/m |
| 流量 | ISO34-1 | 160 kN/m |
| Thermal performance | Test Condition | Test Method | DUPONT TAIWAN/6356 |
|---|---|---|---|
| MD：-40to23°C | ISO11359-2 | 1.6E-04 cm/cm/°C | |
| 1.8MPa,未退火 | ISO75-2/A | 45.0 °C | |
| vicat | -- | ISO306/A50 | 195 °C |
| -- | ISO306/B50 | 100 °C | |
| 0.45MPa,未退火 | ISO75-2/B | 80.0 °C | |
| TD：23to55°C | ASTME831 | 1.7E-04 cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.8E-04 cm/cm/°C | |
| Glass transition temperature 2 | ISO11357-2 | 0.00 °C | |
| melting temperature | ISO11357-3 | 210 °C | |
| brittle temperature | ISO974 | -96.0 °C | |
| MD：-- | ISO11359-2 | 1.9E-04 cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 1.5E-04 cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 5.44E-08 m²/s |