POM TENAC™ 5010 ASAHI JAPAN
330
- Unit Price:US$ 4,751 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:70MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Medium viscosity
- Application Areas:Engine parts｜Cam｜Electronic field｜Electrical field｜Shell｜currency｜Engineering accessories
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D570 | 0.2 % | |
| Shrinkage rate | 1.8-2.2 % | ||
| 1.8-2.2 % | |||
| melt mass-flow rate | ISO 1133 | 22 g/10min | |
| Shrinkage rate | 内部方法 | 1.8-2.2 % | |
| Water absorption rate | ASTM D570 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 94 | |
| ASTM D785 | 120 |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 中粘度 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 69 Mpa | |
| elongation at break | ASTM D638 | 45 % | |
| bending strength | ASTM D790 | 103 Mpa | |
| Flexural modulus | ASTM D790 | 3040 Mpa | |
| Impact strength of cantilever beam gap | ASTM D256 | 69 J/m | |
| Rockwell hardness | ASTM D785 | 120 R | |
| wear resistance | ASTM D1044 | 13 | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 69 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | ASTM D638/ISO 527 | 69 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 45 % | |
| Rockwell hardness | ASTM D785 | 94 | |
| Flexural modulus | ASTM D790/ISO 178 | 3040 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 103 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 3300 Mpa | |
| tensile strength | ISO 527-2 | 72.0 Mpa | |
| ASTM D638 | 72.0 Mpa | ||
| elongation | ASTMD638 | 30 % | |
| Flexural modulus | ASTM D790 | 3040 Mpa | |
| ISO 178 | 3100 Mpa | ||
| bending strength | ASTM D790 | 107 Mpa | |
| Taber abraser | ASTM D1044 | 13.0 mg |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.42 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 22 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 1.0E+16-1.0E+17 ohms | |
| Volume resistivity | ASTM D257 | 1.0E+15-1.0E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 18 KV/mm | |
| dielectric constant | ASTM D150 | 3.80 | |
| Dissipation Factor | ASTM D150 | 7E-03 | |
| arc resistance | ASTM D495 | 250 sec |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | 10 | ||
| Heat distortion temperature | ASTM D648 | 136 °C | |
| ASTM D648 | 172 °C | ||
| UL flame retardant rating | UL 94 | HB | |
| melt mass-flow rate | ASTM D1238 | 22 g/10min | |
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | ASTM D648/ISO 75 | 136(1.8Mpa) ℃（℉） | |
| ASTM D648 | 172 °C | ||
| ISO 75-2/B | 165 °C | ||
| ASTM D648 | 136 °C | ||
| ISO 75-2/A | 105 °C | ||
| Linear coefficient of thermal expansion | ASTMD696 | 1E-04 cm/cm/°C | |
| specific heat | 1470 J/kg/°C | ||
| thermal conductivity | 0.23 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App
Top