Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM 5010 ASAHI JAPAN
TENAC™
Engine parts、Cam、Electronic field、Electrical field、Shell、currency、Engineering accessories
Medium viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | ASAHI JAPAN/5010 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 94 |
| R级 | ASTM D785 | 120 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/5010 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 69 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 103 kg/cm²(MPa)[Lb/in²] | |
| Taber abraser | ASTM D1044 | 13.0 mg | |
| Tensile modulus | ISO 527-2 | 3300 Mpa | |
| elongation | 断裂 | ASTMD638 | 30 % |
| Flexural modulus | ASTM D790/ISO 178 | 3040 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | -- | ASTM D638 | 72.0 Mpa |
| bending strength | ASTM D790 | 107 Mpa | |
| wear resistance | ASTM D1044 | 13 | |
| elongation | ASTM D638/ISO 527 | 45 % | |
| Flexural modulus | -- | ISO 178 | 3100 Mpa |
| Impact strength of cantilever beam gap | ASTM D256 | 69 J/m | |
| Rockwell hardness | ASTM D785 | 94 | |
| elongation at break | ASTM D638 | 45 % | |
| Flexural modulus | ASTM D790 | 3040 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 69 kg/cm²(MPa)[Lb/in²] | |
| ASTM D638 | 69 Mpa | ||
| Rockwell hardness | ASTM D785 | 120 R | |
| tensile strength | 屈服 | ISO 527-2 | 72.0 Mpa |
| Flexural modulus | -- | ASTM D790 | 3040 Mpa |
| Electrical performance | Test Condition | Test Method | ASAHI JAPAN/5010 |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | ASTM D150 | 3.80 |
| Surface Resistivity | ASTM D257 | 1.0E+16-1.0E+17 ohms | |
| Volume resistivity | 23°C | ASTM D257 | 1.0E+15-1.0E+16 ohms·cm |
| Dissipation Factor | 23°C,1MHz | ASTM D150 | 7E-03 |
| dielectric strength | ASTM D149 | 18 KV/mm | |
| arc resistance | ASTM D495 | 250 sec |
| other | Test Condition | Test Method | ASAHI JAPAN/5010 |
|---|---|---|---|
| characteristic | 中粘度 |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/5010 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.42 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 22 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.2 % |
| flammability | Test Condition | Test Method | ASAHI JAPAN/5010 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ASAHI JAPAN/5010 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.8-2.2 % |
| 平行方向 | 1.8-2.2 % | ||
| 垂直方向 | 1.8-2.2 % | ||
| Water absorption rate | ASTM D570 | 0.2 % | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 22 g/10min |
| Water absorption rate | 23°C,24hr,50%RH | ASTM D570 | 0.20 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/5010 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 136 °C |
| melt mass-flow rate | ASTM D1238 | 22 g/10min | |
| Heat distortion temperature | 0.45MPa，HDT | ASTM D648 | 172 °C |
| Linear coefficient of thermal expansion | 10 | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 172 °C |
| HDT | ASTM D648/ISO 75 | 136(1.8Mpa) ℃（℉） | |
| thermal conductivity | 0.23 W/m/K | ||
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 165 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 105 °C | |
| 1.82MPa，HDT | ASTM D648 | 136 °C | |
| specific heat | 1470 J/kg/°C | ||
| Linear coefficient of thermal expansion | MD | ASTMD696 | 1E-04 cm/cm/°C |
| UL flame retardant rating | UL 94 | HB |