PC/ABS CYCOLOY™ 6140 SABIC INNOVATIVE NANSHA
199
- Unit Price:US$ 3,518 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High impact resistance
- Application Areas:Automotive interior parts｜Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.45MPa, Unanealed, 6.40mm | ASTM D648 | 97.0 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 83.0 °C | |
| 1.8MPa, Unanealed, 6.40mm | ASTM D648 | 89.0 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 80.0 °C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 5.5E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 6E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.600mm | UL 94 | V-1 |
| 0.800mm | UL 94 | V-0 | |
| 1.50mm | UL 94 | 5VB | |
| Burning wire flammability index | 0.800mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.00mm | IEC 60695-2-13 | 850 °C |
| 3.00mm | IEC 60695-2-13 | 800 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 50.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
| 23°C | ISO 179/1eA | 10 kJ/m² | |
| -30°C | ASTM D256 | 88 J/m | |
| 23°C | ASTM D256 | 200 J/m | |
| -30°C | ISO 180/1A | 5.0 kJ/m² | |
| 23°C | ISO 180/1A | 10 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 18 g/10min |
| Melt volume flow rate | 220°C/5.0kg | ISO 1133 | 14.0 cm3/10min |
| shrinkage rate | MD:3.20mm | 内部方法 | 0.30-0.50 % |
| TD:3.20mm | 内部方法 | 0.40-0.60 % | |
| 24hr,50%RH | ASTM D570 | 0.010 % | |
| 24hr | ASTM D570 | 0.10 % | |
| Saturation, 23 ° C | ISO 62 | 0.090 % | |
| Balance, 23 ° C, 50% RH | ISO 62 | 0.010 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | 3.5E+15 ohms | |
| volume resistivity | ASTM D257 | 2.7E+16 ohms·cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| --1 | ASTM D638 | 3500 Mpa | |
| yield | ASTM D638 | 65.0 Mpa | |
| ASTM D638 | 65.0 Mpa | ||
| fracture | ASTM D638 | 50.0 Mpa | |
| ISO 527-2/5 | 50.0 Mpa | ||
| yield | ASTM D638 | 4.0 % | |
| ISO 527-2/5 | 3.5 % | ||
| fracture | ASTM D638 | 100 % | |
| ISO 527-2/50 | 15 % | ||
| 50.0mm span | ASTM D790 | 3300 Mpa | |
| --8 | ISO 178 | 3450 Mpa | |
| --9 | ISO 178 | 97.0 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 100 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.