Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS 6140 SABIC INNOVATIVE NANSHA
CYCOLOY™
Automotive interior parts,Electrical applications
Flame retardant,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/6140 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| 23°C | ISO 180/1A | 10 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 50.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
| 23°C | ASTM D256 | 200 J/m | |
| -30°C | ASTM D256 | 88 J/m | |
| ISO 180/1A | 5.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/6140 |
|---|---|---|---|
| fracture | ISO 527-2/50 | 15 % | |
| yield | ASTM D638 | 65.0 Mpa | |
| fracture | ISO 527-2/5 | 50.0 Mpa | |
| yield | ASTM D638 | 4.0 % | |
| fracture | ASTM D638 | 100 % | |
| --9 | ISO 178 | 97.0 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 100 Mpa | |
| yield | ISO 527-2/5 | 3.5 % | |
| --8 | ISO 178 | 3450 Mpa | |
| fracture | ASTM D638 | 50.0 Mpa | |
| 50.0mm span | ASTM D790 | 3300 Mpa | |
| --1 | ASTM D638 | 3500 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/6140 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 2.7E+16 ohms·cm | |
| Surface Resistivity | ASTM D257 | 3.5E+15 ohms |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/6140 |
|---|---|---|---|
| UL flame retardant rating | 0.600mm | UL 94 | V-1 |
| Burning wire flammability index | 0.800mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 0.800mm | UL 94 | V-0 |
| Hot filament ignition temperature | 3.00mm | IEC 60695-2-13 | 800 °C |
| 1.00mm | IEC 60695-2-13 | 850 °C | |
| UL flame retardant rating | 1.50mm | UL 94 | 5VB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/6140 |
|---|---|---|---|
| Melt volume flow rate | 220°C/5.0kg | ISO 1133 | 14.0 cm3/10min |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 18 g/10min |
| 24hr | ASTM D570 | 0.10 % | |
| 24hr,50%RH | ASTM D570 | 0.010 % | |
| Shrinkage rate | MD:3.20mm | 内部方法 | 0.30-0.50 % |
| TD:3.20mm | 内部方法 | 0.40-0.60 % | |
| Saturation, 23 ° C | ISO 62 | 0.090 % | |
| Balance, 23 ° C, 50% RH | ISO 62 | 0.010 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/6140 |
|---|---|---|---|
| 0.45MPa, Unanealed, 6.40mm | ASTM D648 | 97.0 °C | |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 6E-05 cm/cm/°C |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 80.0 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 83.0 °C | |
| 1.8MPa, Unanealed, 6.40mm | ASTM D648 | 89.0 °C | |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 5.5E-05 cm/cm/°C |