LCP

LCP LAPEROS® A130 BK025P DAICEL MALAYSIA

196

Unit Price:US$ 8,768 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Glass fiber reinforced｜Thermal stability｜Chemical resistance
Application Areas:Electrical field｜Electronic field｜Household appliances｜Household appliances
Color:--
Grade:Extrusion grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	29 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0
Extreme Oxygen Index		ISO 4589-2	45 %

mechanical properties	Test Condition	Test Method	Test Result
Compressive stress	1% Strain	ISO 604	100 Mpa
Compressive modulus		ISO 604	14500 Mpa
bending strength	23°C	ISO 178	280 Mpa
Bending modulus	23°C	ISO 178	14500 Mpa
Tensile creep modulus	1000 hr	ISO 899-1	10900 Mpa
Tensile creep modulus	Tensile creep modulus	1 hr	ISO 899-1	12600 Mpa
Tensile strain	Break	ISO 527-2/1A/5	2.1 %
tensile strength	Break	ISO 527-2/1A/5	190 Mpa
Tensile modulus		ISO 527-2/1A	15000 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			150 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.010 %
Hopper temperature			20 to 30 °C
Temperature at the rear of the barrel			270 to 280 °C
Temperature in the middle of the barrel			275 to 285 °C
Temperature at the front of the material cylinder			280 to 290 °C
Spray nozzle temperature			290 to 300 °C
Processing (melt) temperature			285 to 295 °C
Mold temperature			80 to 120 °C
Injection speed			快速
Back pressure			< 3.00 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	2.3E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ISO 11359-2	6.0E-6 cm/cm/°C
Melting temperature		ISO 11357-3	280 °C
Vicat softening temperature		ISO 306/B50	160 °C
Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	190 °C
	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	235 °C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	250 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.040 %
Shrinkage rate	Flow	ISO 294-4	0.20 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	0.40 %

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	100 Hz	IEC 60250	4.20
Dielectric strength		IEC 60243-1	31 KV/mm
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Relative permittivity	1 MHz	IEC 60250	3.70
Dissipation factor	100 Hz	IEC 60250	0.016
Dissipation factor	Dissipation factor	1 MHz	IEC 60250	0.018
Arc resistance		Internal Method	140 sec
Compared to the anti leakage trace index		IEC 60112	PLC 3

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M -Sale	ISO 2039-2	85

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

LCP LAPEROS® A130 BK025P DAICEL MALAYSIA

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet