Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LCP A130 BK025P DAICEL MALAYSIA
LAPEROS®
Electrical field、Electronic field、Household appliances、Household appliances
Flame retardant、Glass fiber reinforced、Thermal stability、Chemical resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DAICEL MALAYSIA/A130 BK025P |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 29 kJ/m² |
| hardness | Test Condition | Test Method | DAICEL MALAYSIA/A130 BK025P |
|---|---|---|---|
| Rockwell hardness | M 计秤 | ISO 2039-2 | 85 |
| Mechanical properties | Test Condition | Test Method | DAICEL MALAYSIA/A130 BK025P |
|---|---|---|---|
| Tensile creep modulus | 1000 hr | ISO 899-1 | 10900 Mpa |
| bending strength | 23°C | ISO 178 | 280 Mpa |
| Compression Modulus | ISO 604 | 14500 Mpa | |
| compression stress | 1% 应变 | ISO 604 | 100 Mpa |
| Flexural modulus | 23°C | ISO 178 | 14500 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 190 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.1 % |
| Tensile modulus | ISO 527-2/1A | 15000 Mpa | |
| Tensile creep modulus | 1 hr | ISO 899-1 | 12600 Mpa |
| Electrical performance | Test Condition | Test Method | DAICEL MALAYSIA/A130 BK025P |
|---|---|---|---|
| relative permittivity | 100 Hz | IEC 60250 | 4.20 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.018 |
| dielectric strength | IEC 60243-1 | 31 KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| arc resistance | 内部方法 | 140 sec | |
| Dissipation Factor | 100 Hz | IEC 60250 | 0.016 |
| relative permittivity | 1 MHz | IEC 60250 | 3.70 |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms |
| flammability | Test Condition | Test Method | DAICEL MALAYSIA/A130 BK025P |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 45 % |
| physical property | Test Condition | Test Method | DAICEL MALAYSIA/A130 BK025P |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.040 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.20 % |
| 横向流量 | ISO 294-4 | 0.40 % |
| Thermal performance | Test Condition | Test Method | DAICEL MALAYSIA/A130 BK025P |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 280 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 250 °C |
| vicat | ISO 306/B50 | 160 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 235 °C |
| 8.0 MPa, 未退火，HDT | ISO 75-2/C | 190 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 6.0E-6 cm/cm/°C |
| 横向 | ISO 11359-2 | 2.3E-5 cm/cm/°C |
| injection | Test Condition | Test Method | DAICEL MALAYSIA/A130 BK025P |
|---|---|---|---|
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.010 % | ||
| Temperature in the middle of the barrel | 275 to 285 °C | ||
| Temperature at the rear of the barrel | 270 to 280 °C | ||
| Processing (melt) temperature | 285 to 295 °C | ||
| Hopper temperature | 20 to 30 °C | ||
| drying temperature | 150 °C | ||
| Temperature at the front of the material cylinder | 280 to 290 °C | ||
| Back pressure | < 3.00 Mpa | ||
| Temperature | 80 to 120 °C | ||
| injection speed | 快速 | ||
| Spray nozzle temperature | 290 to 300 °C |