PC LUPOY® 3010-30 LG CHEM KOREA
201
- Unit Price:US$ 3,288 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High toughness｜High impact resistance｜High mobility｜Good liquidity｜Chemical resistance｜heat-resisting｜High transparency｜Food contact compliance
- Application Areas:Thin walled components｜Electrical field｜Electronic field｜Electrical appliances｜Thin walled components｜Electrical appliances｜Electrical/Electronic Applications
- Color:--
- Grade:High liquidity level
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ASTM D785 | 72 |
| R级 | ASTM D785 | 118 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,退火,4.00mm | ASTM D648 | 139 °C |
| 1.8MPa,未退火,4.00mm | ASTM D648 | 122 °C | |
| 1.8MPa,退火,4.00mm | ASTM D648 | 136 °C | |
| vicat | ASTM D15259 | 144 °C | |
| Ball pressure temperature | IEC 60598-1 | >125 °C | |
| Linear coefficient of thermal expansion | MD：-40到82°C | ASTM D696 | 6.8E-05 cm/cm/°C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | ASTM D1003 | 89.0 % | |
| Haze ratio | ASTM D1003 | 0.70to1.5 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.50mm | UL 94 | V-2 |
| 2.5mm | UL 94 | V-2 | |
| 3.0mm | UL 94 | V-2 | |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 850 °C |
| Limiting Oxygen Index | ASTM D2863 | 26 % | |
| Average degree of combustion | ASTM D635 | 3 CM |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 710 J/m |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | 无断裂 |
| Dart impact | 23°C,3.20mm,TotalEnergy | ASTM D3763 | 87.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | 23°C | ASTM D257 | 2E+17 ohms·cm |
| dielectric strength | ASTM D149 | 17 KV/mm | |
| dielectric constant | 60Hz | ASTM D150 | 3.00 |
| Dissipation Factor | 60Hz | ASTM D150 | 1E-03 |
| Compared to the Leakage Tracking Index (CTI) | 2.00mm | IEC 60112 | PLC 2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 30 g/10min |
| spiral flow length | 3.20 CM | ||
| shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.15 % |
| 平衡,23°C,50%RH | ASTM D570 | 0.32 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服,23°C5 | ASTM D638 | 62.0 Mpa |
| 断裂 | ASTM D638 | 60.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| 断裂 | ASTM D638 | 100 % | |
| flexural modulus | ASTM D790 | 2400 Mpa | |
| bending strength | ASTM D790 | 96.0 Mpa | |
| wear resistance | 雾度变化 | Kg/m | 45 % |
| Tensile modulus | ASTM D638 | 2400 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.