SPS

SPS XAREC™ C142 IDEMITSU JAPAN

418

Unit Price:US$ 2,929 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
31MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜High temperature resistance
Application Areas:Electrical applications｜Household daily necessities
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			玻璃纤维40％增强

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	27 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180	33 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	195 Mpa
Bending modulus		ISO 178	12400 Mpa
Tensile strain	Break	ISO 527-2	1.5 %
tensile strength	Break	ISO 527-2	130 Mpa
Tensile modulus		ISO 527-2	12600 Mpa
bending strength		ASTM D790/ISO 178	195 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	12.4 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	75
tensile strength		ASTM D638/ISO 527	130 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	1.5 %

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	1.5 mm/mm.℃
Combustibility (rate)		UL 94	HB/0.80
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	270 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250 °C
Linear coefficient of thermal expansion	MD：-30to30°C	TMA	1.5E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to30°C	TMA	4E-05 cm/cm/°C
RTI Elec		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C
RTI Str		UL 746	50.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.020 %
Shrinkage rate	MD	Internal Method	0.10-0.40 %
Shrinkage rate	Shrinkage rate	TD	Internal Method	0.50-0.80 %
Water absorption rate		ASTM D570/ISO 62	0.02 %
density		ASTM D792/ISO 1183	1.36

Electrical performance	Test Condition	Test Method	Test Result
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI)3	IEC 60112	PLC 1
Dissipation factor	1MHz	IEC 60250	<1.0E-3
Dielectric constant	1MHz	IEC 60250	3.00
Dielectric strength		ASTM D149	45 KV/mm
Volume resistivity		ASTM D257/IEC 60093	>1.0*10^16 Ω.cm
Arc resistance		ASTM D495/IEC 60112	120
Volume resistivity		IEC 60093	>1.0E+16 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.