Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
SPS C142 IDEMITSU JAPAN
XAREC™
Electrical applications、Household daily necessiti
Glass fiber reinforced、High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/C142 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 33 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 27 kJ/m² |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/C142 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 45 KV/mm | |
| dielectric constant | 1MHz | IEC 60250 | 3.00 |
| Compared to the Leakage Tracking Index (CTI) | CTI)3 | IEC 60112 | PLC 1 |
| arc resistance | ASTM D495 | PLC6 | |
| ASTM D495/IEC 60112 | 120 | ||
| Volume resistivity | ASTM D257/IEC 60093 | >1.0*10^16 Ω.cm | |
| Dissipation Factor | 1MHz | IEC 60250 | <1.0E-3 |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/C142 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 195 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ISO 527-2 | 12600 Mpa | |
| Flexural modulus | ASTM D790/ISO 178 | 12.4 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 195 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| Flexural modulus | ISO 178 | 12400 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 130 Mpa |
| elongation at break | ASTM D638/ISO 527 | 1.5 % | |
| Rockwell hardness | ASTM D785 | 75 | |
| tensile strength | ASTM D638/ISO 527 | 130 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | IDEMITSU JAPAN/C142 |
|---|---|---|---|
| characteristic | 玻璃纤维40％增强 |
| Physical properties | Test Condition | Test Method | IDEMITSU JAPAN/C142 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.36 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/C142 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/C142 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.10-0.40 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.020 % |
| Shrinkage rate | TD | 内部方法 | 0.50-0.80 % |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/C142 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB/0.80 | |
| Linear coefficient of thermal expansion | TD：-30to30°C | TMA | 4E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 270 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 250 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | TMA | 1.5E-05 cm/cm/°C |
| RTI Imp | UL 746 | 50.0 °C | |
| RTI Str | UL 746 | 50.0 °C | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.5 mm/mm.℃ | |
| RTI Elec | UL 746 | 50.0 °C |