Material Description
- Material Properties:Glass fiber reinforced｜Flame retardant｜Filler: Glass mineral｜55% filler by weight
- Application Areas:Electrical applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 东丽法 | 110 | ||
| Shrinkage rate | 东丽法 | 0.15 % | |
| 东丽法 | 0.55 % | ||
| 内部方法 | 0.75 % | ||
| 内部方法 | 0.16 % | ||
| Water absorption rate | ISO 62 | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 122 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ASTM D-570 | 0.02 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| BarFlowLength | 内部方法 | 115 mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ASTM D-790 | 190 Mpa | |
| tensile strength | ASTM D-638 | 145 Mpa | |
| limiting pv value | 东丽法 | 815 KJ/m | |
| tensile strength | ASTM D-638 | 1.3 % | |
| coefficient of friction | ASTM D-1894 | 0.28 | |
| abrasion | ASTM D-1044 | 70 mg/1000回 | |
| bending strength | ASTM D-790 | 15.1 GPa | |
| elongation at break | ASTM D-732 | 65 | |
| Impact strength of cantilever beam gap | ASTM D-256 | 100 J/m | |
| ASTM D-256 | 25 KJ/m | ||
| Shore hardness | ASTM D-785 | 122 洛氏 | |
| tensile strength | ISO 527-2 | 170 Mpa | |
| Tensile strain | ISO 527-2 | 1.3 % | |
| Flexural modulus | ISO 178 | 18500 Mpa | |
| bending strength | ISO 178 | 255 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 30 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Inherent resistance of volume | ASTM D-257 | 10 Ω.m | |
| arc resistance | ASTM D-495 | 128 秒 | |
| Induced positive connection | ASTM D-150 | 0.002 | |
| dielectric constant | ASTM D-150 | 5.0 | |
| dielectric strength | ASTM D-149 | 15 MV/m | |
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | 22 KV/mm | |
| dielectric constant | IEC 60250 | 4.90 | |
| Dissipation Factor | IEC 60250 | 2E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| combustibility | UL -94 | V-0 | |
| Linear coefficient of thermal expansion | ASTM D-696 | 1.7 | |
| ASTM D-696 | 2.5 | ||
| melting temperature | DSC | 278 °C | |
| Heat distortion temperature | ASTM D-648 | >260 °C | |
| ISO 75-2/A | 260 °C | ||
| melting temperature | ISO 11357-3 | 278 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.8E-05 cm/cm/°C | |
| ISO 11359-2 | 3E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.