LCP ZENITE® 6130 DUPONT USA

331

Unit Price:US$ 5,430 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
40MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜High temperature resistance｜Antistatic｜Glass fiber reinforced
Application Areas:Aerospace｜Electrical field｜Electronic field｜Household appliances｜Household appliances
Color:--
Grade:Injection grade

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			30%玻纤增强
machinability	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	Across Flow		0.5	%
Shrinkage rate	Shrinkage rate	Flow		0	%
Mold temperature			90	°C
Melt Temperature			335	°C
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate			0.002	%
CTI UL standard value			4
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790/ISO 178	190	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	11000	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	165	kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	13000	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	2.7	%
Charpy Notched Impact Strength		ASTM D256/ISO 179	30	kg·cm/cm(J/M)ft·lb/in
	Charpy Notched Impact Strength		ASTM D256/ISO 179	40	kg·cm/cm(J/M)ft·lb/in
	Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	35	kg·cm/cm(J/M)ft·lb/in
bending strength			170	Mpa
tensile strength			2.7	%
Bending modulus			12	GPa
Rockwell hardness			108	R
tensile strength			150	Mpa
Impact strength of cantilever beam gap			120	J/m
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	HDT	ASTM D648/ISO 75	300	℃（℉）
Hot deformation temperature	Hot deformation temperature	0.46Mpa		277	ºC
Linear coefficient of thermal expansion			1.3(3.7)	10-5k
Hot deformation temperature	1.82Mpa		265	ºC
Combustibility			V-0（0.2)
Hot deformation temperature	HDT	ASTM D648/ISO 75	268	℃（℉）
Melting temperature			335	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Fiberglass content			30	%
density		ASTM D792/ISO 1183	1620
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant			3.9
Dielectric strength			26	MV/m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Zhonghexin	US$ 6100 /MT
Guangzhou HuShang Chemical	US$ 8770 /MT

Supplier Join

Get App

Top

LCP ZENITE® 6130 DUPONT USA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index