PC IUPILON™ KH3520UR MITSUBISHI ENGINEERING JAPAN
220
- Unit Price:US$ 9,650 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:105.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High hardness｜transparent
- Application Areas:Electric tool casing｜optical glass
- Color:--
- Grade:--
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| notes | 硬度高 | ||
| characteristic | 硬度高(3H) 透明度好 | ||
| Color | 透明 | ||
| purpose | 用于抗刮花外观部件.5G产品.电器电子产品 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-2 | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 123 ℃（℉） |
| HDT | ASTM D648/ISO 75 | 103 ℃（℉） |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmittance | ASTM D1003/ISO 13468 | 全光线.透光率89 % |
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dry conditions | 80烘 5-7hr | ||
| process temperature | 240-280 °C | ||
| mold temperature | 60-80 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.17 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 10.5 g/10min | |
| ASTM D1238/ISO 1133 | 11.5 g/10min | ||
| Water absorption rate | ASTM D570/ISO 62 | 0.19 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 200 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 370 kg·cm/cm(J/M)ft·lb/in | ||
| Elongation at break | ASTM D638/ISO 527 | 33 % | |
| Tensile modulus | ASTM D638/ISO 527 | 2900MPa kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 82.0 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 6.0 % | |
| Rockwell hardness | ASTM D785 | 0.3HRC | |
| flexural modulus | ASTM D790/ISO 178 | 2900MPa kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 113MPa kg/cm²(MPa)[Lb/in²] | |
| Elongation at break | ASTM D638/ISO 527 | 33 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.