PC KH3520UR MITSUBISHI ENGINEERING JAPAN
IUPILON™
Electric tool casing,optical glass
High hardness,transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/KH3520UR |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 113MPa kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2900MPa kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 6.0 % | |
| Tensile modulus | ASTM D638/ISO 527 | 2900MPa kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 370 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 33 % | |
| Rockwell hardness | ASTM D785 | 0.3HRC | |
| tensile strength | ASTM D638/ISO 527 | 82.0 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/KH3520UR |
|---|---|---|---|
| characteristic | 硬度高(3H) 透明度好 | ||
| notes | 硬度高 | ||
| Color | 透明 | ||
| purpose | 用于抗刮花外观部件.5G产品.电器电子产品 |
| optical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/KH3520UR |
|---|---|---|---|
| transmittance | ASTM D1003/ISO 13468 | 全光线.透光率89 % |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/KH3520UR |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.17 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 11.5 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.19 % |
| processability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/KH3520UR |
|---|---|---|---|
| process temperature | 240-280 °C | ||
| Dry conditions | 80烘 5-7hr | ||
| Temperature | 60-80 °C |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/KH3520UR |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-2 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 103 ℃（℉） |