PA66

PA66 Leona™ 1402G ASAHI JAPAN

236

Unit Price:US$ 3,673 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
99MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Moderate heat resistance｜Thermal stability｜Creep resistance｜Fatigue resistance｜high strength｜High rigidity
Application Areas:Automotive sector｜component｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

other	Test Condition	Test Method	Test Result
characteristic			玻纤增强含热稳定增强

Other performance	Test Condition	Test Method	Test Result
Extreme Oxygen Index	干	ASTM D-2863	23 %

machinability	Test Condition	Test Method	Test Result
Dry conditions			2-3小时 80-90度

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	湿		1.7 %

mechanical properties	Test Condition	Test Method	Test Result
flexural coefficient	干(湿)	ASTM D-790	9.3(6.3) GPa
tensile strength	干(湿)	ASTM D-638	186(132) Mpa
bending strength	干(湿)	ASTM D-790	289(216) Mpa
Rockwell hardness	干(湿)	ASTM D-785	96(75) M Scale
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	127(147) J/m
Elongation at Break	干(湿)	ASTM D-638	3(5) %
Rockwell hardness	干(湿)	ASTM D-785	120(112) R scale

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.82MPa,干	ASTM D-648	250 °C
UL flame retardant rating	干	UL 94	HB
Hot deformation temperature	0.46MPa,干	ASTM D-648	260 °C
thermal conductivity	干		0.3 W/(m.K)
Linear coefficient of thermal expansion	干	ASTM D-696	3 ×10-5/K
specific heat	干		1590 J/(kg.k)
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	260 ℃（℉）
Hot deformation temperature	Hot deformation temperature	HDT	ASTM D648/ISO 75	264 ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	干	旭化成方法	0.4/0.9 %
Wear factor	湿	ASTM D-1044	15 ×10-6kg/1000times

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Leona™ 1402G ASAHI JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet