Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 1402G ASAHI JAPAN
Leona™
Automotive sector,component,Electronic field,Electrical field
Moderate heat resistance,Thermal stability,Creep resistance,Fatigue resistance,high strength,High rigidity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | ASAHI JAPAN/1402G |
|---|---|---|---|
| Limiting Oxygen Index | 干 | ASTM D-2863 | 23 % |
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/1402G |
|---|---|---|---|
| Water absorption rate | 湿 | 1.7 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/1402G |
|---|---|---|---|
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(112) R scale |
| 干(湿) | ASTM D-785 | 96(75) M Scale | |
| bending strength | 干(湿) | ASTM D-790 | 289(216) Mpa |
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 127(147) J/m |
| flexural coefficient | 干(湿) | ASTM D-790 | 9.3(6.3) GPa |
| tensile strength | 干(湿) | ASTM D-638 | 186(132) Mpa |
| elongation at break | 干(湿) | ASTM D-638 | 3(5) % |
| other | Test Condition | Test Method | ASAHI JAPAN/1402G |
|---|---|---|---|
| characteristic | 玻纤增强含热稳定增强 |
| processability | Test Condition | Test Method | ASAHI JAPAN/1402G |
|---|---|---|---|
| Dry conditions | 2-3小时 80-90度 |
| physical property | Test Condition | Test Method | ASAHI JAPAN/1402G |
|---|---|---|---|
| Wear factor | 湿 | ASTM D-1044 | 15 ×10-6kg/1000times |
| Shrinkage rate | 干 | 旭化成方法 | 0.4/0.9 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/1402G |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| specific heat | 干 | 1590 J/(kg.k) | |
| Heat distortion temperature | 1.82MPa,干，HDT | ASTM D-648 | 250 °C |
| HDT | ASTM D648/ISO 75 | 264 ℃（℉） | |
| 0.46MPa,干，HDT | ASTM D-648 | 260 °C | |
| thermal conductivity | 干 | 0.3 W/(m.K) | |
| UL flame retardant rating | 干 | UL 94 | HB |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 3 ×10-5/K |