PBT VALOX™ 310SE0-BK SABIC INNOVATIVE JAPAN
210
- Unit Price:US$ 3,224 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:33MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant
- Application Areas:Spool｜Shell｜switch｜Home appliance components｜Electronic field｜Electrical field｜currency
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 120 |
| ball-indentation hardness | H 358/30 | ISO 2039-1 | 105 Mpa |
| Rockwell hardness | R级 | ASTM D785 | 117 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 162 °C |
| 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距10 | ISO 75-2/Be | 150 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 74.0 °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 71.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距10 | ISO 75-2/Ae | 60.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9 | ISO 75-2/Af | 73.0 °C | |
| vicat | -- | ASTM D152511 | 170 °C |
| -- | ISO 306/A50 | 212 °C | |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 7.9E-5 cm/cm/°C |
| 流动 : 60 到 138°C | ASTM E831 | 1.3E-4 cm/cm/°C | |
| 流动 : -40 到 40°C | ISO 11359-2 | 7.6E-5 cm/cm/°C | |
| 流动 : 23 到 60°C | ISO 11359-2 | 1.0E-4 cm/cm/°C | |
| 横向 : -40 到 40°C | ASTM E831 | 7.9E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 7.3E-5 cm/cm/°C | |
| 横向 : 23 到 60°C | ISO 11359-2 | 1.0E-4 cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.24 W/m/K | |
| RTI Elec | UL 746 | 120 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 140 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 154 °C |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 54.4 °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 8.1E-05 cm/cm/°C |
| MD：60to138°C | ASTME831 | 1.4E-04 cm/cm/°C | |
| RTI Elec | UL 746 | 120 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI Str | UL 746 | 140 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.71 mm | UL 94 | V-0 |
| 3.0 mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ISO 4589-2 | 30 % | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 无断裂 |
| -30°C9 | ISO 180/1U | 无断裂 | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 200 J |
| 23°C | ASTM D3029 | 40.7 J | |
| 23°C6 | ASTM D3029 | 40.7 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.710 cm³/g | |
| melt mass-flow rate | 250°C/2.16 kg | ASTM D1238 | 8.6 g/10 min |
| Melt volume flow rate | 250°C/2.16 kg | ISO 1133 | 8.00 cm3/10min |
| shrinkage rate | 流动 2 | 内部方法 | 1.1 - 1.8 % |
| 流动 : 0.750 到 2.30 mm | 内部方法 | 0.90 - 1.6 % | |
| 流动 : 3.20 mm | 内部方法 | 1.5 - 2.3 % | |
| 流动 : 2.30 到 4.60 mm | 内部方法 | 1.5 - 2.3 % | |
| 横向流动 2 | 内部方法 | 0.90 - 1.9 % | |
| 横向流动 : 0.750 到 2.30 mm | 内部方法 | 1.0 - 1.7 % | |
| 横向流动 : 2.30 到 4.60 mm | 内部方法 | 1.6 - 2.4 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.36 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.080 % | |
| Specific volume | ASTM D792 | 0.770 cm³/g | |
| shrinkage rate | MD：--2 | 内部方法 | 0.90-1.6 % |
| MD：--3 | 内部方法 | 1.5-2.3 % | |
| TD：--2 | 内部方法 | 1.0-1.7 % | |
| TD：--3 | 内部方法 | 1.6-2.4 % | |
| Water absorption rate | 24hr | ASTM D570 | 0.080 % |
| melt viscosity | 内部方法 | 600 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 24 KV/mm |
| 3.20 mm, in Air | ASTM D149 | 18 KV/mm | |
| 0.800 mm, 在油中 | IEC 60243-1 | 35 KV/mm | |
| 1.00 mm12 | IEC 60243-1 | 18 KV/mm | |
| 1.60 mm, 在油中 | IEC 60243-1 | 25 KV/mm | |
| 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm | |
| relative permittivity | 50 Hz | IEC 60250 | 2.90 |
| 60 Hz | IEC 60250 | 2.90 | |
| 100 Hz | IEC 60250 | 3.10 | |
| 1 MHz | IEC 60250 | 2.80 | |
| Dissipation Factor | 50 Hz | IEC 60250 | 1.0E-3 |
| 60 Hz | IEC 60250 | 1.0E-3 | |
| 100 Hz | IEC 60250 | 2.0E-3 | |
| 1 MHz | IEC 60250 | 0.013 | |
| arc resistance | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| -- | IEC 60112 | V | |
| 解决方案 B | IEC 60112 | V | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| High Voltage Arc Resistance Index (HVAR) (PLC) | UL 746 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| dielectric constant | 100Hz | ASTM D150 | 3.30 |
| 1MHz | ASTM D150 | 3.10 | |
| Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
| 1MHz | ASTM D150 | 0.020 | |
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| volume resistivity | ASTM D257 | >4.0E+16 ohms·cm | |
| dielectric strength | 1.60mm,inAir | ASTM D149 | 23 KV/mm |
| 1.60mm,在油中 | ASTM D149 | 23 KV/mm | |
| 3.20mm,inAir | ASTM D149 | 16 KV/mm | |
| 3.20mm,在油中 | ASTM D149 | 16 KV/mm |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 80 % | ||
| Temperature at the rear of the barrel | 230 to 250 °C | ||
| Temperature in the middle of the barrel | 240 to 255 °C | ||
| Temperature at the front of the material cylinder | 245 to 260 °C | ||
| Spray nozzle temperature | 240 to 255 °C | ||
| Processing (melt) temperature | 245 to 260 °C | ||
| mold temperature | 50 to 75 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 50 to 100 rpm | ||
| Exhaust hole depth | 0.013 to 0.025 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --3 | ASTM D638 | 2820 Mpa |
| -- | ISO 527-2/1 | 2800 Mpa | |
| tensile strength | 屈服4 | ASTM D638 | 58.0 Mpa |
| 屈服 | ISO 527-2/50 | 58.0 Mpa | |
| 断裂4 | ASTM D638 | 52.0 Mpa | |
| 断裂 | ISO 527-2/50 | 40.0 Mpa | |
| elongation | 屈服4 | ASTM D638 | 5.0 % |
| 屈服 | ISO 527-2/50 | 5.0 % | |
| 断裂4 | ASTM D638 | 18 % | |
| 断裂 | ISO 527-2/50 | 18 % | |
| flexural modulus | 50.0 mm 跨距5 | ASTM D790 | 2620 Mpa |
| --6 | ISO 178 | 2600 Mpa | |
| bending strength | --6,7 | ISO 178 | 90.0 Mpa |
| 屈服, 50.0 mm 跨距5 | ASTM D790 | 101 Mpa | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 19.0 mg |
| tensile strength | 屈服 | ASTM D638 | 51.7 Mpa |
| Break | ASTM D638 | 51.7 Mpa | |
| elongation | 断裂 | ASTM D638 | 300 % |
| flexural modulus | 50.0mmSpan | ASTM D790 | 2340 Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 82.7 Mpa |
| Break,50.0mmSpan | ASTM D790 | 82.7 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.