PBT 310SE0-BK SABIC INNOVATIVE JAPAN
VALOX™
Spool、Shell、switch、Home appliance components、Electronic field、Electrical field、currency
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310SE0-BK |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Suspended wall beam without notch impact strength | -30°C9 | ISO 180/1U | 无断裂 |
| Dart impact | 23°C6 | ASTM D3029 | 40.7 J |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 200 J |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 无断裂 |
| Dart impact | 23°C | ASTM D3029 | 40.7 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310SE0-BK |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 120 |
| ball-indentation hardness | H 358/30 | ISO 2039-1 | 105 Mpa |
| Rockwell hardness | R级 | ASTM D785 | 117 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310SE0-BK |
|---|---|---|---|
| tensile strength | 屈服4 | ASTM D638 | 58.0 Mpa |
| elongation | 断裂4 | ASTM D638 | 18 % |
| Tensile modulus | --3 | ASTM D638 | 2820 Mpa |
| Flexural modulus | 50.0 mm 跨距5 | ASTM D790 | 2620 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 18 % |
| bending strength | Break,50.0mmSpan | ASTM D790 | 82.7 Mpa |
| --6,7 | ISO 178 | 90.0 Mpa | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 19.0 mg |
| Flexural modulus | --6 | ISO 178 | 2600 Mpa |
| bending strength | 屈服, 50.0 mm 跨距5 | ASTM D790 | 101 Mpa |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 2340 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 40.0 Mpa |
| 屈服 | ISO 527-2/50 | 58.0 Mpa | |
| elongation | 断裂 | ASTM D638 | 300 % |
| tensile strength | Break | ASTM D638 | 51.7 Mpa |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 82.7 Mpa |
| elongation | 屈服 | ISO 527-2/50 | 5.0 % |
| 屈服4 | ASTM D638 | 5.0 % | |
| tensile strength | 断裂4 | ASTM D638 | 52.0 Mpa |
| 屈服 | ASTM D638 | 51.7 Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 2800 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310SE0-BK |
|---|---|---|---|
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 24 KV/mm |
| relative permittivity | 50 Hz | IEC 60250 | 2.90 |
| Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
| dielectric strength | 3.20mm,在油中 | ASTM D149 | 16 KV/mm |
| relative permittivity | 1 MHz | IEC 60250 | 2.80 |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 B | IEC 60112 | V |
| -- | IEC 60112 | V | |
| Volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| dielectric strength | 1.00 mm12 | IEC 60243-1 | 18 KV/mm |
| Dissipation Factor | 60 Hz | IEC 60250 | 1.0E-3 |
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| arc resistance | ASTM D495 | PLC 5 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| Volume resistivity | ASTM D257 | >4.0E+16 ohms·cm | |
| dielectric strength | 0.800 mm, 在油中 | IEC 60243-1 | 35 KV/mm |
| Dissipation Factor | 1MHz | ASTM D150 | 0.020 |
| 100 Hz | IEC 60250 | 2.0E-3 | |
| 50 Hz | IEC 60250 | 1.0E-3 | |
| dielectric constant | 1MHz | ASTM D150 | 3.10 |
| 100Hz | ASTM D150 | 3.30 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| relative permittivity | 100 Hz | IEC 60250 | 3.10 |
| dielectric strength | 1.60 mm, 在油中 | IEC 60243-1 | 25 KV/mm |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.013 |
| dielectric strength | 1.60mm,inAir | ASTM D149 | 23 KV/mm |
| 3.20 mm, in Air | ASTM D149 | 18 KV/mm | |
| 3.20mm,inAir | ASTM D149 | 16 KV/mm | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm |
| relative permittivity | 60 Hz | IEC 60250 | 2.90 |
| High Voltage Arc Resistance Index (HVAR) (PLC) | UL 746 | PLC 6 | |
| dielectric strength | 1.60mm,在油中 | ASTM D149 | 23 KV/mm |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310SE0-BK |
|---|---|---|---|
| UL flame retardant rating | 0.71 mm | UL 94 | V-0 |
| 3.0 mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ISO 4589-2 | 30 % | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310SE0-BK |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16 kg | ASTM D1238 | 8.6 g/10 min |
| Shrinkage rate | 流动 2 | 内部方法 | 1.1 - 1.8 % |
| Water absorption rate | 24hr | ASTM D570 | 0.080 % |
| Shrinkage rate | MD：--2 | 内部方法 | 0.90-1.6 % |
| 流动 : 0.750 到 2.30 mm | 内部方法 | 0.90 - 1.6 % | |
| MD：--3 | 内部方法 | 1.5-2.3 % | |
| Melt volume flow rate | 250°C/2.16 kg | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | TD：--2 | 内部方法 | 1.0-1.7 % |
| 流动 : 2.30 到 4.60 mm | 内部方法 | 1.5 - 2.3 % | |
| 横向流动 : 0.750 到 2.30 mm | 内部方法 | 1.0 - 1.7 % | |
| TD：--3 | 内部方法 | 1.6-2.4 % | |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.080 % |
| Shrinkage rate | 横向流动 2 | 内部方法 | 0.90 - 1.9 % |
| 横向流动 : 2.30 到 4.60 mm | 内部方法 | 1.6 - 2.4 % | |
| Specific volume | ASTM D792 | 0.770 cm³/g | |
| melt viscosity | 内部方法 | 600 Pa·s | |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 1.5 - 2.3 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.36 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310SE0-BK |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 7.9E-5 cm/cm/°C |
| vicat | -- | ASTM D152511 | 170 °C |
| Linear coefficient of thermal expansion | 流动 : 23 到 60°C | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI | UL 746 | 140 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 162 °C |
| thermal conductivity | ISO 8302 | 0.24 W/m/K | |
| Linear coefficient of thermal expansion | 流动 : 60 到 138°C | ASTM E831 | 1.3E-4 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距10，HDT | ISO 75-2/Be | 150 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 71.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDT | ISO 75-2/Af | 73.0 °C | |
| 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 74.0 °C | |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 54.4 °C | |
| Linear coefficient of thermal expansion | 横向 : 23 到 60°C | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距10，HDT | ISO 75-2/Ae | 60.0 °C |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 7.3E-5 cm/cm/°C |
| MD：60to138°C | ASTME831 | 1.4E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 154 °C |
| RTI Str | UL 746 | 140 °C | |
| vicat | -- | ISO 306/A50 | 212 °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 8.1E-05 cm/cm/°C |
| 流动 : -40 到 40°C | ISO 11359-2 | 7.6E-5 cm/cm/°C | |
| RTI Imp | UL 746 | 120 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 7.9E-5 cm/cm/°C |
| RTI Elec | UL 746 | 120 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/310SE0-BK |
|---|---|---|---|
| screw speed | 50 to 100 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 245 to 260 °C | ||
| drying temperature | 120 °C | ||
| Suggested injection volume | 40 to 80 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 240 to 255 °C | ||
| Temperature at the rear of the barrel | 230 to 250 °C | ||
| Exhaust hole depth | 0.013 to 0.025 mm | ||
| Temperature at the front of the material cylinder | 245 to 260 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 50 to 75 °C | ||
| Spray nozzle temperature | 240 to 255 °C |