Plastic Raw Materials
TPV

TPV Santoprene™ 101-80 CELANESE USA

375
  • Unit Price:US$ 4,775 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    39MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High temperature resistance
  • Application Areas:household electrical appliances｜Automotive Applications｜Electrical applications｜Pipe fittings｜Washer｜Application in the automotive field｜Parts under the hood of a car｜Home appliance components｜Consumer product application field｜diaphragm｜Electrical components｜Outdoor applications｜packing
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.0mmUL 94HB
UL flame retardant rating1.5mmUL 94HB
UL flame retardant rating3.0mmUL 94HB
elastomerTest ConditionTest MethodTest Result
tensile strengthBreak,23°CISO 3711.1 Mpa
tensile strengthBreak,23°C，横向FlowASTM D41211.1 Mpa
Tensile stress100%Strain,23°C，横向FlowISO 374.70 Mpa
Tensile stress100%Strain,23°C，横向FlowASTM D4124.70 Mpa
Permanent compression deformation125°C,70hrISO 81547 %
Permanent compression deformation70°C,22hrISO 81541 %
Permanent compression deformation125°C,70hrASTM D395B47 %
Permanent compression deformation70°C,22hrASTM D395B41 %
tear strength23°C，Across Flow (Across Flow)ISO 34-135 kN/m
tear strength23°C，横向FlowASTM D62435.0 kN/m
elongationBreak,23°C，Across FlowISO 37540 %
elongationBreak,23°C，Across FlowASTM D412540 %
thermal performanceTest ConditionTest MethodTest Result
RTI Str3.0mmUL 74695.0 °C
RTI Str1.5mmUL 74690.0 °C
RTI Str1.0mmUL 74690.0 °C
RTI ElecUL 74690.0 °C
Brittle temperatureISO 812-60.0 °C
Brittle temperatureASTM D746-60.0 °C
Physical propertiesTest ConditionTest MethodTest Result
Resistance to cleaning agentsUL 749f3
Resistance to cleaning agentsISO 188f4
Outdoor applicabilityUL 746Cf1
Electrical performanceTest ConditionTest MethodTest Result
Hot wire ignition1.0mmUL 746PLC 4
Dielectric strength23°C,2.00mmASTM D14930 KV/mm
Dielectric constant23°C,1.98mmASTM D1502.60
Dielectric constant23°C,1.98mmIEC 602502.60
Compared to the anti leakage trace indexCTIUL 746PLC 0
High arc combustion indexHAIUL 746PLC 0
High voltage arc tracing ratePLCUL 746
High voltage arc tracing rateHVTRUL 746PLC 1
Hot wire ignition1.5mmUL 746PLC 3
Hot wire ignition3.0mmUL 746PLC 2
Hot wire ignition3.0mmUL 746PLC 2
hardnessTest ConditionTest MethodTest Result
Shore hardnessShoreA,15Sec,23°CISO 86886
agingTest ConditionTest MethodTest Result
Change rate of ultimate elongation in air150°C,168hrASTM D573-12 %
Hardness change rate in the airShoreA,150°C,168hrASTM D5735.0
Shore hardnessShoreA,150°C,168hrISO 1885.0
Change rate of tensile strength in air150°C,168hrISO 188-5.0 %
Change rate of tensile strength in air150°C,168hrASTM D573-5.0 %
Change rate of tensile strength in air23°C,168hr,inAceticAcidASTM D4717.0 %
Change rate of tensile strength in air23°C,168hr,inHydrochloricAcid,10%ASTM D4715.0 %
Change rate of tensile strength in air23°C,168hr,inCyclohexaneASTM D47119 %
Change rate of ultimate elongation in air23°C,168hr,inHydrochloricAcid,10%ASTM D4714.0 %
Change rate of ultimate elongation in air23°C,168hr,inIsopropylAlcoholASTM D47114 %
Change rate of ultimate elongation in air23°C,168hr,inMethylethylketoneASTM D47116 %
Change rate of ultimate elongation in air23°C,168hr,inSodiumChloride,15%ASTM D4712.0 %
Change rate of ultimate elongation in air23°C,168hr,inSodiumHydroxide,50%ASTM D4714.0 %
Change rate of ultimate elongation in air23°C,168hr,inSulfuricAcid,98%ASTM D471-26 %
Change rate of ultimate elongation in air23°C,168hr,inTrichloroethyleneASTM D47112 %
Change rate of ultimate elongation in air100°C,168hr,inDeionizedWaterASTM D471-6.0 %
Change rate of ultimate elongation in air100°C,168hr,inIRM903OilASTM D471-46 %
Change rate of ultimate elongation in air125°C,70hr,inIRM903OilASTM D471-43 %
Change rate of tensile strength in air23°C,168hr,inEthanol,95%ASTM D471-3.0 %
Change rate of tensile strength in air23°C,168hr,inIsopropylAlcoholASTM D47126 %
Change rate of tensile strength in air23°C,168hr,inMethylethylketoneASTM D47130 %
Change rate of tensile strength in air23°C,168hr,inSodiumChloride,15%ASTM D4713.0 %
Change rate of tensile strength in air23°C,168hr,inSodiumHydroxide,50%ASTM D4716.0 %
Change rate of tensile strength in air23°C,168hr,inSulfuricAcid,98%ASTM D471-16 %
Change rate of tensile strength in air23°C,168hr,inTrichloroethyleneASTM D47130 %
Change rate of tensile strength in air100°C,168hr,inDeionizedWaterASTM D471-1.0 %
Change rate of tensile strength in air100°C,168hr,inIRM903OilASTM D471-25 %
Change rate of ultimate elongation in air125°C,168hr,inIRM903OilASTM D471-52 %
Tensile stress change rate23°C,168hr,inAceticAcid，BreakISO 18174.0 %
Tensile stress change rate23°C,168hr,inHydrochloricAcid,10%，BreakISO 18174.0 %
Tensile stress change rate23°C,168hr,inIsopropylAlcohol，BreakISO 181714 %
Change rate of ultimate elongation in air23°C,168hr,inCyclohexaneASTM D47112 %
Tensile stress change rate23°C,168hr,inCyclohexane，BreakISO 181712 %
Tensile stress change rate23°C,168hr,inDetergent(Tide),2.5%，BreakISO 18170.0 %
Tensile stress change rate23°C,168hr,inEthanol,95%，BreakISO 18170.0 %
Tensile stress change rate23°C,168hr,inMethylethylketone，BreakISO 181716 %
Tensile stress change rate23°C,168hr,inSodiumChloride,15%，BreakISO 18172.0 %
Tensile stress change rate23°C,168hr,inSodiumHydroxide,50%，BreakISO 18174.0 %
Change rate of tensile strength in air23°C,168hr,inSulfuricAcid,98%ISO 1817-16 %
Change rate of tensile strength in air23°C,168hr,inTrichloroethyleneISO 181730 %
Change rate of tensile strength in air100°C,168hr,inDeionizedWaterISO 1817-1.0 %
Change rate of tensile strength in air100°C,168hr,inIRM903OilISO 1817-25 %
Change rate of tensile strength in air125°C,70hr,inIRM903OilISO 1817-25 %
Change rate of tensile strength in air125°C,168hr,inIRM903OilISO 1817-30 %
Change rate of ultimate elongation in air23°C,168hr,inAceticAcidASTM D4714.0 %
Change rate of ultimate elongation in air23°C,168hr,inDetergent(Tide),2.5%ASTM D4710.0 %
Change rate of ultimate elongation in air23°C,168hr,inEthanol,95%ASTM D4710.0 %
Change rate of tensile strength in air125°C,70hr,inIRM903OilASTM D471-25 %
Change rate of tensile strength in air125°C,168hr,inIRM903OilASTM D471-30 %
Change rate of tensile strength in air23°C,168hr,inAceticAcidISO 18177.0 %
Change rate of tensile strength in air23°C,168hr,inCyclohexaneISO 181719 %
Change rate of tensile strength in air23°C,168hr,inEthanol,95%ISO 1817-3.0 %
Change rate of tensile strength in air23°C,168hr,inHydrochloricAcid,10%ISO 18175.0 %
Change rate of tensile strength in air23°C,168hr,inIsopropylAlcoholISO 181726 %
Change rate of tensile strength in air23°C,168hr,inSodiumHydroxide,50%ISO 18176.0 %
Change rate of tensile strength in air23°C,168hr,inMethylethylketoneISO 181730 %
Change rate of tensile strength in air23°C,168hr,inSodiumChloride,15%ISO 18173.0 %
Quality change rate100°C,168hr,inIRM903OilISO 181757 %
Shore hardnessShoreA,100°C,168hr,inIRM903OilISO 1817-17
Shore hardnessShoreA,125°C,168hr,inIRM903OilISO 1817-20
Quality change rate23°C,168hr,inAceticAcidASTM D4713.3 %
Quality change rate23°C,168hr,inCyclohexaneASTM D471-3.4 %
Quality change rate23°C,168hr,inDetergent(Tide),2.5%ASTM D4710.40 %
Quality change rate23°C,168hr,inEthanol,95%ASTM D471-0.40 %
Quality change rate23°C,168hr,inHydrochloricAcid,10%ASTM D4710.20 %
Quality change rate23°C,168hr,inIsopropylAlcoholASTM D471-11 %
Quality change rate23.0°C,168hr,inAceticAcidISO 18173.3 %
Tensile stress change rate23°C,168hr,inSulfuricAcid,98%，BreakISO 1817-26 %
Tensile stress change rate23°C,168hr,inTrichloroethylene，BreakISO 181712 %
Tensile stress change rate100°C,168hr,inDeionizedWater，BreakISO 1817-6.0 %
Tensile stress change rate100°C,168hr,inIRM903Oil，BreakISO 1817-46 %
Tensile stress change rate125°C,70hr,inIRM903Oil，BreakISO 1817-43 %
Tensile stress change rate125°C,168hr,inIRM903Oil，BreakISO 1817-52 %
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inAceticAcidASTM D471-1.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inAceticAcidASTM D471-1.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inCyclohexaneASTM D471-13
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inDetergent(Tide),2.5%ASTM D4711.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inEthanol,95%ASTM D471-1.0
Shore hardnessShoreA,23°C,168hr,inTrichloroethyleneISO 1817-3.0
Shore hardnessShoreA,100°C,168hr,inDeionizedWaterISO 1817-2.0
Volume change125°C,70hr,在IRM903油中ISO 181764 %
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inHydrochloricAcid,10%ASTM D471-1.0
Quality change rate125°C,168hr,inIRM903OilISO 181766 %
Volume change125°C,70hr,在IRM903油中ASTM D47164 %
Quality change rate23°C,168hr,inSodiumHydroxide,50%ASTM D471-0.10 %
Quality change rate100°C,168hr,inIRM903OilASTM D47157 %
Quality change rate23°C,168hr,inSulfuricAcid,98%ASTM D4712.3 %
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inIsopropylAlcoholASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inMethylethylketoneASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inSodiumChloride,15%ASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inSodiumHydroxide,50%ASTM D4710.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inSulfuricAcid,98%ASTM D4711.0
Change rate of hardness (Shore) in the airShoreA,23°C,168hr,inTrichloroethyleneASTM D471-3.0
Change rate of hardness (Shore) in the airShoreA,100°C,168hr,inDeionizedWaterASTM D471-2.0
Quality change rate23.0°C,168hr,inSodiumChloride,15%ISO 18170.20 %
Quality change rate23.0°C,168hr,inDetergent(Tide),2.5%ISO 18170.40 %
Change rate of hardness (Shore) in the airShoreA,100°C,168hr,inIRM903OilASTM D471-17
Change rate of hardness (Shore) in the airShoreA,125°C,168hr,inIRM903OilASTM D471-20
Shore hardnessShoreA,23°C,168hr,inAceticAcidISO 1817-1.0
Shore hardnessShoreA,23°C,168hr,inCyclohexaneISO 1817-13
Shore hardnessShoreA,23°C,168hr,inDetergent(Tide),2.5%ISO 18171.0
Shore hardnessShoreA,23°C,168hr,inEthanol,95%ISO 1817-1.0
Shore hardnessShoreA,23°C,168hr,inHydrochloricAcid,10%ISO 1817-1.0
Shore hardnessShoreA,23°C,168hr,inIsopropylAlcoholISO 18170.0
Shore hardnessShoreA,23°C,168hr,inMethylethylketoneISO 18170.0
Shore hardnessShoreA,23°C,168hr,inSodiumChloride,15%ISO 18170.0
Shore hardnessShoreA,23°C,168hr,inSodiumHydroxide,50%ISO 18170.0
Quality change rate125°C,168hr,inIRM903OilASTM D47166 %
Quality change rate23.0°C,168hr,inMethylethylketoneISO 1817-19 %
Quality change rate23.0°C,168hr,inIsopropylAlcoholISO 1817-11 %
Quality change rate23.0°C,168hr,inTrichloroethyleneISO 1817-6.0 %
Quality change rate23.0°C,168hr,inCyclohexaneISO 1817-3.4 %
Quality change rate23.0°C,168hr,inEthanol,95%ISO 1817-0.40 %
Quality change rate23.0°C,168hr,inSodiumHydroxide,50%ISO 1817-0.10 %
Quality change rate23.0°C,168hr,inHydrochloricAcid,10%ISO 18170.20 %
Quality change rate23°C,168hr,inTrichloroethyleneASTM D471-6.0 %
Quality change rate100°C,168hr,inDeionizedWaterASTM D4713.1 %
Shore hardnessShoreA,23°C,168hr,inSulfuricAcid,98%ISO 18171.0
Quality change rate23°C,168hr,inMethylethylketoneASTM D471-19 %
Quality change rate23°C,168hr,inSodiumChloride,15%ASTM D4710.20 %
Quality change rate23.0°C,168hr,inSulfuricAcid,98%ISO 18172.3 %
Quality change rate100°C,168hr,inDeionizedWaterISO 18173.1 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Contact Us

Get App

Top