TPV 101-80 CELANESE USA
Santoprene™
household electrical appl、Automotive Applications、Electrical applications、Pipe fittings、Washer、Application in the automo、Parts under the hood of a、Home appliance components、Consumer product applicat、diaphragm、Electrical components、Outdoor applications、packing
High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | CELANESE USA/101-80 |
|---|---|---|---|
| Shore hardness | 邵氏A,15秒,23°C | ISO 868 | 86 |
| Electrical performance | Test Condition | Test Method | CELANESE USA/101-80 |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| dielectric strength | 23°C,2.00mm | ASTM D149 | 30 KV/mm |
| Hot wire ignition (HWI) | 1.0mm | UL 746 | PLC 4 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 3 |
| 3.0mm | UL 746 | PLC 2 | |
| dielectric constant | 23°C,1.98mm | IEC 60250 | 2.60 |
| 23°C,1.98mm | ASTM D150 | 2.60 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | PLC | UL 746 |
| flammability | Test Condition | Test Method | CELANESE USA/101-80 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.0mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | CELANESE USA/101-80 |
|---|---|---|---|
| Resistance to cleaning agents | UL 749 | f3 | |
| Outdoor applicability | UL 746C | f1 | |
| Resistance to cleaning agents | ISO 188 | f4 |
| elastomer | Test Condition | Test Method | CELANESE USA/101-80 |
|---|---|---|---|
| elongation | 断裂,23°C，横向 | ASTM D412 | 540 % |
| Tensile stress | 100%应变,23°C，横向流量 | ISO 37 | 4.70 Mpa |
| tensile strength | 断裂,23°C，横向流量 | ASTM D412 | 11.1 Mpa |
| elongation | 断裂,23°C，横向 | ISO 37 | 540 % |
| tear strength | 23°C，Across Flow (横向) | ISO 34-1 | 35 kN/m |
| tensile strength | Break,23°C | ISO 37 | 11.1 Mpa |
| compression set | 70°C,22hr | ASTM D395B | 41 % |
| 70°C,22hr | ISO 815 | 41 % | |
| 125°C,70hr | ISO 815 | 47 % | |
| tear strength | 23°C，横向流量 | ASTM D624 | 35.0 kN/m |
| Tensile stress | 100%应变,23°C，横向流量 | ASTM D412 | 4.70 Mpa |
| compression set | 125°C,70hr | ASTM D395B | 47 % |
| aging | Test Condition | Test Method | CELANESE USA/101-80 |
|---|---|---|---|
| mass change fraction | 23°C,168hr,inMethylethylketone | ASTM D471 | -19 % |
| Tensile stress change rate | 23°C,168hr,inAceticAcid，断裂 | ISO 1817 | 4.0 % |
| mass change fraction | 23°C,168hr,inDetergent(Tide),2.5% | ASTM D471 | 0.40 % |
| Tensile stress change rate | 23°C,168hr,inIsopropylAlcohol，断裂 | ISO 1817 | 14 % |
| Shore hardness | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 0.0 |
| Change rate of tensile strength in air | 23°C,168hr,inIsopropylAlcohol | ISO 1817 | 26 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inSulfuricAcid,98% | ASTM D471 | 1.0 |
| ShoreA,23°C,168hr,inSodiumChloride,15% | ASTM D471 | 0.0 | |
| Change rate of ultimate elongation in air | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 2.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inAceticAcid | ISO 1817 | 7.0 % |
| 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 3.0 % | |
| Shore hardness | ShoreA,100°C,168hr,inDeionizedWater | ISO 1817 | -2.0 |
| mass change fraction | 23°C,168hr,inCyclohexane | ASTM D471 | -3.4 % |
| 23°C,168hr,inEthanol,95% | ASTM D471 | -0.40 % | |
| Change rate of tensile strength in air | 125°C,168hr,inIRM903Oil | ASTM D471 | -30 % |
| 125°C,168hr,inIRM903Oil | ISO 1817 | -30 % | |
| mass change fraction | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -0.10 % |
| Shore hardness | ShoreA,23°C,168hr,inSodiumChloride,15% | ISO 1817 | 0.0 |
| Change rate of hardness (Shore) in the air | ShoreA,125°C,168hr,inIRM903Oil | ASTM D471 | -20 |
| mass change fraction | 23.0°C,168hr,inSodiumChloride,15% | ISO 1817 | 0.20 % |
| Tensile stress change rate | 23°C,168hr,inSulfuricAcid,98%，断裂 | ISO 1817 | -26 % |
| mass change fraction | 23°C,168hr,inTrichloroethylene | ASTM D471 | -6.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 5.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inMethylethylketone | ASTM D471 | 0.0 |
| Change rate of tensile strength in air | 150°C,168hr | ISO 188 | -5.0 % |
| Tensile stress change rate | 125°C,70hr,inIRM903Oil，断裂 | ISO 1817 | -43 % |
| Shore hardness | ShoreA,23°C,168hr,inDetergent(Tide),2.5% | ISO 1817 | 1.0 |
| Change rate of tensile strength in air | 100°C,168hr,inIRM903Oil | ISO 1817 | -25 % |
| Tensile stress change rate | 100°C,168hr,inIRM903Oil，断裂 | ISO 1817 | -46 % |
| mass change fraction | 100°C,168hr,inIRM903Oil | ASTM D471 | 57 % |
| 23.0°C,168hr,inTrichloroethylene | ISO 1817 | -6.0 % | |
| Change rate of tensile strength in air | 23°C,168hr,inIsopropylAlcohol | ASTM D471 | 26 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inTrichloroethylene | ASTM D471 | -3.0 |
| mass change fraction | 23.0°C,168hr,inSodiumHydroxide,50% | ISO 1817 | -0.10 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inEthanol,95% | ASTM D471 | -1.0 |
| Shore hardness | ShoreA,23°C,168hr,inEthanol,95% | ISO 1817 | -1.0 |
| ShoreA,125°C,168hr,inIRM903Oil | ISO 1817 | -20 | |
| Change rate of tensile strength in air | 100°C,168hr,inDeionizedWater | ISO 1817 | -1.0 % |
| Change rate of ultimate elongation in air | 100°C,168hr,inIRM903Oil | ASTM D471 | -46 % |
| 23°C,168hr,inEthanol,95% | ASTM D471 | 0.0 % | |
| volume change | 125°C,70hr,在IRM903油中 | ASTM D471 | 64 % |
| Shore hardness | ShoreA,23°C,168hr,inAceticAcid | ISO 1817 | -1.0 |
| Change rate of ultimate elongation in air | 150°C,168hr | ASTM D573 | -12 % |
| Change rate of hardness (Shore) in the air | ShoreA,100°C,168hr,inIRM903Oil | ASTM D471 | -17 |
| mass change fraction | 23.0°C,168hr,inMethylethylketone | ISO 1817 | -19 % |
| Change rate of tensile strength in air | 23°C,168hr,inMethylethylketone | ASTM D471 | 30 % |
| 23°C,168hr,inSulfuricAcid,98% | ISO 1817 | -16 % | |
| 125°C,70hr,inIRM903Oil | ISO 1817 | -25 % | |
| Change rate of ultimate elongation in air | 23°C,168hr,inMethylethylketone | ASTM D471 | 16 % |
| Tensile stress change rate | 23°C,168hr,inTrichloroethylene，断裂 | ISO 1817 | 12 % |
| mass change fraction | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 0.20 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 6.0 % |
| 23°C,168hr,inAceticAcid | ASTM D471 | 7.0 % | |
| Tensile stress change rate | 125°C,168hr,inIRM903Oil，断裂 | ISO 1817 | -52 % |
| Shore hardness | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | -1.0 |
| ShoreA,100°C,168hr,inIRM903Oil | ISO 1817 | -17 | |
| Change rate of tensile strength in air | 23°C,168hr,inTrichloroethylene | ASTM D471 | 30 % |
| volume change | 125°C,70hr,在IRM903油中 | ISO 1817 | 64 % |
| Shore hardness | ShoreA,23°C,168hr,inIsopropylAlcohol | ISO 1817 | 0.0 |
| ShoreA,150°C,168hr | ISO 188 | 5.0 | |
| Tensile stress change rate | 100°C,168hr,inDeionizedWater，断裂 | ISO 1817 | -6.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 4.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 0.0 |
| Change rate of tensile strength in air | 150°C,168hr | ASTM D573 | -5.0 % |
| mass change fraction | 23.0°C,168hr,inDetergent(Tide),2.5% | ISO 1817 | 0.40 % |
| Tensile stress change rate | 23°C,168hr,inSodiumChloride,15%，断裂 | ISO 1817 | 2.0 % |
| mass change fraction | 23°C,168hr,inAceticAcid | ASTM D471 | 3.3 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inIsopropylAlcohol | ASTM D471 | 14 % |
| mass change fraction | 23.0°C,168hr,inAceticAcid | ISO 1817 | 3.3 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -1.0 |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 5.0 % |
| Tensile stress change rate | 23°C,168hr,inDetergent(Tide),2.5%，断裂 | ISO 1817 | 0.0 % |
| Change rate of ultimate elongation in air | 125°C,168hr,inIRM903Oil | ASTM D471 | -52 % |
| Tensile stress change rate | 23°C,168hr,inEthanol,95%，断裂 | ISO 1817 | 0.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inTrichloroethylene | ASTM D471 | 12 % |
| Tensile stress change rate | 23°C,168hr,inCyclohexane，断裂 | ISO 1817 | 12 % |
| Change rate of tensile strength in air | 23°C,168hr,inTrichloroethylene | ISO 1817 | 30 % |
| Shore hardness | ShoreA,23°C,168hr,inMethylethylketone | ISO 1817 | 0.0 |
| mass change fraction | 125°C,168hr,inIRM903Oil | ISO 1817 | 66 % |
| Change rate of tensile strength in air | 23°C,168hr,inCyclohexane | ASTM D471 | 19 % |
| 23°C,168hr,inEthanol,95% | ASTM D471 | -3.0 % | |
| 100°C,168hr,inDeionizedWater | ASTM D471 | -1.0 % | |
| mass change fraction | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | 2.3 % |
| Change rate of tensile strength in air | 100°C,168hr,inIRM903Oil | ASTM D471 | -25 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inCyclohexane | ASTM D471 | 12 % |
| Tensile stress change rate | 23°C,168hr,inSodiumHydroxide,50%，断裂 | ISO 1817 | 4.0 % |
| Change rate of ultimate elongation in air | 100°C,168hr,inDeionizedWater | ASTM D471 | -6.0 % |
| mass change fraction | 23.0°C,168hr,inIsopropylAlcohol | ISO 1817 | -11 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inDetergent(Tide),2.5% | ASTM D471 | 0.0 % |
| mass change fraction | 23.0°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 0.20 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumChloride,15% | ISO 1817 | 3.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inDetergent(Tide),2.5% | ASTM D471 | 1.0 |
| Tensile stress change rate | 23°C,168hr,inHydrochloricAcid,10%，断裂 | ISO 1817 | 4.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inCyclohexane | ISO 1817 | 19 % |
| mass change fraction | 23.0°C,168hr,inCyclohexane | ISO 1817 | -3.4 % |
| Change rate of tensile strength in air | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | -16 % |
| mass change fraction | 23°C,168hr,inIsopropylAlcohol | ASTM D471 | -11 % |
| Hardness change rate in the air | ShoreA,150°C,168hr | ASTM D573 | 5.0 |
| mass change fraction | 23.0°C,168hr,inSulfuricAcid,98% | ISO 1817 | 2.3 % |
| 100°C,168hr,inIRM903Oil | ISO 1817 | 57 % | |
| Shore hardness | ShoreA,23°C,168hr,inSulfuricAcid,98% | ISO 1817 | 1.0 |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 6.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 4.0 % |
| mass change fraction | 100°C,168hr,inDeionizedWater | ASTM D471 | 3.1 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | -26 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inAceticAcid | ASTM D471 | -1.0 |
| Change rate of ultimate elongation in air | 125°C,70hr,inIRM903Oil | ASTM D471 | -43 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inIsopropylAlcohol | ASTM D471 | 0.0 |
| Change rate of ultimate elongation in air | 23°C,168hr,inAceticAcid | ASTM D471 | 4.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,100°C,168hr,inDeionizedWater | ASTM D471 | -2.0 |
| Change rate of tensile strength in air | 125°C,70hr,inIRM903Oil | ASTM D471 | -25 % |
| mass change fraction | 23.0°C,168hr,inEthanol,95% | ISO 1817 | -0.40 % |
| Shore hardness | ShoreA,23°C,168hr,inTrichloroethylene | ISO 1817 | -3.0 |
| Tensile stress change rate | 23°C,168hr,inMethylethylketone，断裂 | ISO 1817 | 16 % |
| mass change fraction | 100°C,168hr,inDeionizedWater | ISO 1817 | 3.1 % |
| Shore hardness | ShoreA,23°C,168hr,inCyclohexane | ISO 1817 | -13 |
| mass change fraction | 125°C,168hr,inIRM903Oil | ASTM D471 | 66 % |
| Change rate of tensile strength in air | 23°C,168hr,inMethylethylketone | ISO 1817 | 30 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inCyclohexane | ASTM D471 | -13 |
| mass change fraction | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 0.20 % |
| Change rate of tensile strength in air | 23°C,168hr,inEthanol,95% | ISO 1817 | -3.0 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/101-80 |
|---|---|---|---|
| brittle temperature | ISO 812 | -60.0 °C | |
| RTI Str | 1.0mm | UL 746 | 90.0 °C |
| brittle temperature | ASTM D746 | -60.0 °C | |
| RTI Str | 1.5mm | UL 746 | 90.0 °C |
| 3.0mm | UL 746 | 95.0 °C | |
| RTI Elec | UL 746 | 90.0 °C |