PC LEXAN™  EXL1414T-WH9G396 SABIC INNOVATIVE US

200
  • Unit Price:US$ 2,840 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    31MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Low temperature resistancetransparentProcessabilityModerate liquidityDuctilitycopolymer
  • Application Areas:Electrical fieldElectronic fieldHousehold appliancesHousehold appliancesBottle cap
  • Color:--
  • Grade:--

Technical Data Sheet Compare

hardnessTest ConditionTest MethodTest Result
Rockwell hardnessL 计秤ISO 2039-287
thermal performanceTest ConditionTest MethodTest Result
Heat Deflection Temperature1.8 MPa, 未退火, 3.20 mmASTM D648120 °C
Heat Deflection Temperature1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9ISO 75-2/Af116 °C
vicat--ASTM D152510138 °C
vicat--ISO 306/B120139 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
Linear coefficient of thermal expansion流动 : -40 到 95°CASTM E8316.7E-5 cm/cm/°C
Linear coefficient of thermal expansion流动 : 23 到 80°CISO 11359-26.7E-5 cm/cm/°C
Linear coefficient of thermal expansion横向 : -40 到 95°CASTM E8318.0E-5 cm/cm/°C
Linear coefficient of thermal expansion横向 : 23 到 80°CISO 11359-28.0E-5 cm/cm/°C
RTI ElecUL 746130 °C
RTIUL 746130 °C
optical performance Test ConditionTest MethodTest Result
transmissivity2540 µmASTM D100382.0 %
Haze ratio2540 µmASTM D10033.0 %
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.8 mmUL 94HB
UL flame retardant rating3.0 mmUL 94V-2
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
Hot filament ignition temperature0.8 mmIEC 60695-2-13850 °C
Hot filament ignition temperature3.0 mmIEC 60695-2-13850 °C
Impact resistanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA60 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact-30°C, Total EnergyASTM D376377.0 J
Dart impact23°C, Total EnergyASTM D376375.0 J
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2 kgASTM D123810 g/10 min
Melt volume flow rate300°C/1.2 kgISO 11339.00 cm3/10min
shrinkage rate流动 : 3.20 mm内部方法0.40 - 0.80 %
shrinkage rate横向流动 : 3.20 mm内部方法0.40 - 0.80 %
Water absorption rate饱和, 23°CISO 620.12 %
Water absorption rate平衡, 23°C, 50% RHISO 620.090 %
Electrical performanceTest ConditionTest MethodTest Result
Surface ResistivityASTM D257> 1.0E+15 ohms
volume resistivityASTM D257> 1.0E+15 ohms·cm
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel270 to 295 °C
Temperature in the middle of the barrel280 to 305 °C
Temperature at the front of the material cylinder295 to 315 °C
Spray nozzle temperature290 to 310 °C
Processing (melt) temperature295 to 315 °C
mold temperature70 to 95 °C
Back pressure0.300 to 0.700 Mpa
screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--2ASTM D6382180 Mpa
Tensile modulus--ISO 527-2/12300 Mpa
tensile strength屈服3ASTM D63857.0 Mpa
tensile strength屈服ISO 527-2/5056.0 Mpa
tensile strength断裂3ASTM D63859.0 Mpa
tensile strength断裂ISO 527-2/5055.0 Mpa
elongation屈服3ASTM D6385.6 %
elongation屈服ISO 527-2/505.4 %
elongation断裂3ASTM D638120 %
elongation断裂ISO 527-2/50110 %
flexural modulus50.0 mm 跨距4ASTM D7902180 Mpa
flexural modulus--5ISO 1782120 Mpa
bending strength--5,6ISO 17888.0 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D79092.0 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.