PC EXL1414T-WH9G396 SABIC INNOVATIVE US
LEXAN™ 
Electrical field、Electronic field、Household appliances、Household appliances、Bottle cap
Low temperature resistanc、transparent、Processability、Moderate liquidity、Ductility、copolymer
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL1414T-WH9G396
Charpy Notched Impact Strength23°CISO 179/1eA70 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA60 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact-30°C, Total EnergyASTM D376377.0 J
23°C, Total EnergyASTM D376375.0 J
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/EXL1414T-WH9G396
Rockwell hardnessL 计秤ISO 2039-287
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/EXL1414T-WH9G396
Tensile modulus--2ASTM D6382180 Mpa
tensile strength 屈服3ASTM D63857.0 Mpa
elongation断裂3ASTM D638120 %
断裂ISO 527-2/50110 %
Flexural modulus--5ISO 1782120 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D79092.0 Mpa
--5,6ISO 17888.0 Mpa
Flexural modulus50.0 mm 跨距4ASTM D7902180 Mpa
tensile strength 断裂ISO 527-2/5055.0 Mpa
屈服ISO 527-2/5056.0 Mpa
elongation屈服ISO 527-2/505.4 %
屈服3ASTM D6385.6 %
tensile strength 断裂3ASTM D63859.0 Mpa
Tensile modulus--ISO 527-2/12300 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL1414T-WH9G396
Volume resistivityASTM D257> 1.0E+15 ohms·cm
Surface ResistivityASTM D257> 1.0E+15 ohms
optical performance Test ConditionTest MethodSABIC INNOVATIVE US/EXL1414T-WH9G396
transmissivity2540 µmASTM D100382.0 %
Haze ratio2540 µmASTM D10033.0 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/EXL1414T-WH9G396
UL flame retardant rating3.0 mmUL 94V-2
Hot filament ignition temperature0.8 mmIEC 60695-2-13850 °C
3.0 mmIEC 60695-2-13850 °C
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
UL flame retardant rating0.8 mmUL 94HB
physical property Test ConditionTest MethodSABIC INNOVATIVE US/EXL1414T-WH9G396
Water absorption rate平衡, 23°C, 50% RHISO 620.090 %
Shrinkage rate横向流动 : 3.20 mm内部方法0.40 - 0.80 %
Melt volume flow rate300°C/1.2 kgISO 11339.00 cm3/10min
melt mass-flow rate300°C/1.2 kgASTM D123810 g/10 min
Shrinkage rate流动 : 3.20 mm内部方法0.40 - 0.80 %
Water absorption rate饱和, 23°CISO 620.12 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/EXL1414T-WH9G396
vicat--ISO 306/B120139 °C
--ASTM D152510138 °C
Linear coefficient of thermal expansion流动 : -40 到 95°CASTM E8316.7E-5 cm/cm/°C
横向 : 23 到 80°CISO 11359-28.0E-5 cm/cm/°C
流动 : 23 到 80°CISO 11359-26.7E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDTISO 75-2/Af116 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
RTIUL 746130 °C
Linear coefficient of thermal expansion横向 : -40 到 95°CASTM E8318.0E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D648120 °C
RTI ElecUL 746130 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE US/EXL1414T-WH9G396
screw speed40 to 70 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature295 to 315 °C
drying temperature120 °C
Suggested injection volume40 to 60 %
drying time3.0 to 4.0 hr
Temperature in the middle of the barrel280 to 305 °C
Temperature at the rear of the barrel270 to 295 °C
Exhaust hole depth0.025 to 0.076 mm
Temperature at the front of the material cylinder295 to 315 °C
Back pressure0.300 to 0.700 Mpa
Temperature70 to 95 °C
Spray nozzle temperature290 to 310 °C