Material Properties:High rigidity｜High impact｜Filler: Glass fiber reinforced material｜40% filler by weight
Application Areas:Electronic and Electrical Applications｜Automotive sector
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
melt mass-flow rate		ISO 1133	1.8 g/10min
Melt volume flow rate		ISO 1133	1.00 cm3/10min
Shrinkage rate			0.35 %
Water absorption rate		ISO 62	0.060 %
Water absorption rate	Water absorption rate		ISO 62	0.70 %

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

Mechanical properties	Test Method	Test Result
bending strength	ISO 178	215 Mpa
Tensile modulus	ISO 527-2	20900 Mpa
tensile strength	ISO 527-2	130 Mpa
Tensile strain	ISO 527-2	0.60 %
Flexural modulus	ISO 178	22200 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179	12 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC 60093	5E+03 ohms
Volume resistivity		IEC 60093	3E+02 ohms·cm

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	234 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	223 °C
Linear coefficient of thermal expansion		ISO 11359-2	8E-06 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	4E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.