Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA/MXD6 4511 MITSUBISHI ENGINEERING JAPAN
RENY™
Electronic and Electrical、Automotive sector
High rigidity、High impact、Filler: Glass fiber reinf、40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/4511 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 12 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/4511 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 20900 Mpa | |
| bending strength | ISO 178 | 215 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 0.60 % |
| Flexural modulus | ISO 178 | 22200 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 130 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/4511 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 3E+02 ohms·cm | |
| Surface Resistivity | IEC 60093 | 5E+03 ohms |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/4511 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/4511 |
|---|---|---|---|
| Shrinkage rate | 0.35 % | ||
| Melt volume flow rate | 280°C/3.8kg | ISO 1133 | 1.00 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.70 % |
| 饱和,23°C | ISO 62 | 0.060 % | |
| melt mass-flow rate | 280°C/3.8kg | ISO 1133 | 1.8 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/4511 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 234 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 223 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-06 cm/cm/°C |
| TD | ISO 11359-2 | 4E-05 cm/cm/°C |