PA/ABS

PA/ABS Terblend®N N NM-19 BASF USA

331

Unit Price:US$ 2,931 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
95MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:UV resistance｜Easy to process｜High mobility｜High impact resistance
Application Areas:Automotive sector｜Automotive interior parts｜sporting goods｜Low temperature applications
Color:--
Grade:Injection grade

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
Bending modulus		ISO 178	1500 Mpa
bending strength		ISO 178	50.0 Mpa
Tensile modulus		ISO 527-2	1600 Mpa
tensile strength	Yield,23°C	ISO 527-2	35.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	3.4 %
tensile strength	Yield,23°C	ISO 527-2	43.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	3.5 %
Bending modulus		ISO 178	1800 Mpa
bending strength		ISO 178	62.0 Mpa
Tensile modulus		ISO 527-2	2000 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	80.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	58.0 °C
Vicat softening temperature	--	ISO 306/A50	165 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	91.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	65.0 °C
Vicat softening temperature	--	ISO 306/A50	160 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	102 °C
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	85.0 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	240°C/10.0kg	ISO 1133	25.0 cm3/10min
Shrinkage rate		ISO 294-4	0.80 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.1 %
Melt Volume Flow Rate (MVR)	240°C/10.0kg	ISO 1133	30.0 cm3/10min
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.2 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	1E+14 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Relative permittivity	1MHz	IEC 60250	2.90
Dissipation factor	1MHz	IEC 60250	0.015
Compared to the anti leakage trace index		IEC 60112	PLC 0

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ISO 2039-2	103
Ball Pressure Test		ISO 2039-1	86.0 Mpa

film	Test Condition	Test Method	Test Result
elongation	Break	ISO 527-3	>50 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA/ABS Terblend®N N NM-19 BASF USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet