Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA/ABS N NM-19 BASF USA
Terblend®N
Automotive sector、Automotive interior parts、sporting goods、Low temperature applicati
UV resistance、Easy to process、High mobility、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | BASF USA/N NM-19 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 103 |
| ball-indentation hardness | ISO 2039-1 | 86.0 Mpa |
| film | Test Condition | Test Method | BASF USA/N NM-19 |
|---|---|---|---|
| elongation | 断裂 | ISO 527-3 | >50 % |
| Mechanical properties | Test Condition | Test Method | BASF USA/N NM-19 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2000 Mpa | |
| bending strength | ISO 178 | 62.0 Mpa | |
| Flexural modulus | ISO 178 | 1800 Mpa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 43.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 3.5 % |
| Electrical performance | Test Condition | Test Method | BASF USA/N NM-19 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| physical property | Test Condition | Test Method | BASF USA/N NM-19 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.80 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.2 % |
| Melt volume flow rate | 240°C/10.0kg | ISO 1133 | 30.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF USA/N NM-19 |
|---|---|---|---|
| vicat | -- | ISO 306/A50 | 160 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 65.0 °C |
| vicat | -- | ISO 306/B50 | 102 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-04 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ISO 75-2/B | 80.0 °C |
| 0.45MPa,Annealed，HDT | ISO 75-2/B | 85.0 °C |