PPO NORYL™ V0150B-701 SABIC INNOVATIVE JAPAN

337

Unit Price:US$ 3,680 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Dimensional stability｜Low water absorption｜Non enhanced｜Low temperature impact resistance
Application Areas:Shell｜Solar junction box｜Outdoor applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	50.0	J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	13	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	5.0	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	14	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	775	°C
Burning wire flammability index	1.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	775	°C
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.0mm	UL 94	5VA
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	775	°C
Extreme Oxygen Index		ISO 4589-2	32	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ASTM D638	7.0	%
Tensile strain	Break	ISO 527-2/50	10	%
Tensile strain	Tensile strain	Yield	ISO 527-2/50	4.0	%
elongation	Yield	ASTM D638	5.0	%
tensile strength	Break	ISO 527-2/50	55.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	70.0	Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	35.0	mg
bending strength	Yield,50.0mmSpan	ASTM D790	105	Mpa
bending strength	bending strength		ISO 178	110	Mpa
tensile strength	Break	ASTM D638	60.0	Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	70.0	Mpa
Bending modulus	50.0mmSpan	ASTM D790	2550	Mpa
Bending modulus	Bending modulus		ISO 178	2400	Mpa
Tensile modulus		ASTM D638	2500	Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	2500	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	140°C12	IEC 60695-10-2	Pass
Ball Pressure Test	Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Vicat softening temperature	--	ISO 306/B120	155	°C
	Vicat softening temperature	--	ISO 306/B50	145	°C
		Vicat softening temperature	--	ISO 306/A50	160	°C
		Vicat softening temperature	Vicat softening temperature		ASTM D152511	155	°C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	130	°C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	135	°C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	140	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.5E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：23to80°C	ISO 11359-2	7E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	7.5E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to80°C	ISO 11359-2	9E-05	cm/cm/°C
thermal conductivity		ISO 8302	0.27	W/m/K
RTI Elec		UL 746	110	°C
RTI Imp		UL 746	105	°C
RTI Str		UL 746	115	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	MD：--2	Internal Method	0.50-0.70	%
melt mass-flow rate	280°C/5.0kg	ASTM D1238	3.5	g/10min
Melt Volume Flow Rate (MVR)	300°C/5.0kg	ISO 1133	10.0	cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Water absorption rate	Saturation,23°C	ISO 62	0.18	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.060	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	0.800mm,in Oil	IEC 60243-1	33	KV/mm
	Dielectric strength	1.60mm,in Oil	IEC 60243-1	26	KV/mm
	Dielectric strength	Dielectric strength	3.20mm,in Oil	IEC 60243-1	16	KV/mm
Relative permittivity	50Hz	IEC 60250	2.80
	Relative permittivity	60Hz	IEC 60250	2.80
	Relative permittivity	Relative permittivity	1MHz	IEC 60250	2.70
Dissipation factor	50Hz	IEC 60250	9E-04
	Dissipation factor	60Hz	IEC 60250	9E-04
	Dissipation factor	Dissipation factor	1MHz	IEC 60250	3E-03
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	1E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	H358/30	ISO 2039-1	113	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPO NORYL™ V0150B-701 SABIC INNOVATIVE JAPAN

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index