Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO V0150B-701 SABIC INNOVATIVE JAPAN
NORYL™ 
Shell、Solar junction box、Outdoor applications
Dimensional stability、Low water absorption、Non enhanced、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE JAPAN/V0150B-701
Charpy Notched Impact Strength23°CISO 179/1eA14 kJ/m²
Dart impact23°C,TotalEnergyASTM D376350.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA5.0 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A5.0 kJ/m²
23°CISO 180/1A13 kJ/m²
hardnessTest ConditionTest MethodSABIC INNOVATIVE JAPAN/V0150B-701
ball-indentation hardnessH358/30ISO 2039-1113 Mpa
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE JAPAN/V0150B-701
Tensile modulusISO 527-2/12500 Mpa
elongation屈服ASTM D6385.0 %
Flexural modulus50.0mmSpanASTM D7902550 Mpa
Tensile strain屈服ISO 527-2/504.0 %
tensile strength 断裂ISO 527-2/5055.0 Mpa
屈服ISO 527-2/5070.0 Mpa
Tensile modulusASTM D6382500 Mpa
elongation断裂ASTM D6387.0 %
bending strengthYield,50.0mmSpanASTM D790105 Mpa
tensile strength BreakASTM D63860.0 Mpa
bending strengthISO 178110 Mpa
Taber abraser1000Cycles,1000g,CS-17转轮内部方法35.0 mg
Flexural modulusISO 1782400 Mpa
tensile strength 屈服ASTM D63870.0 Mpa
Tensile strain断裂ISO 527-2/5010 %
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE JAPAN/V0150B-701
relative permittivity60HzIEC 602502.80
dielectric strength0.800mm,在油中IEC 60243-133 KV/mm
relative permittivity50HzIEC 602502.80
Volume resistivityIEC 600931E+15 ohms·cm
dielectric strength1.60mm,在油中IEC 60243-126 KV/mm
3.20mm,在油中IEC 60243-116 KV/mm
relative permittivity1MHzIEC 602502.70
Surface ResistivityIEC 60093>1.0E+15 ohms
Dissipation Factor50HzIEC 602509E-04
60HzIEC 602509E-04
1MHzIEC 602503E-03
Compared to the Leakage Tracking Index (CTI)IEC 60112 V
flammabilityTest ConditionTest MethodSABIC INNOVATIVE JAPAN/V0150B-701
Hot filament ignition temperature2.0mmIEC 60695-2-13775 °C
UL flame retardant rating2.0mmUL 945VA
Hot filament ignition temperature3.0mmIEC 60695-2-13775 °C
1.0mmIEC 60695-2-13775 °C
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
UL flame retardant rating1.5mmUL 94V-0
Limiting Oxygen IndexISO 4589-232 %
physical property Test ConditionTest MethodSABIC INNOVATIVE JAPAN/V0150B-701
Shrinkage rateMD：3.20mm内部方法0.50-0.70 %
Melt volume flow rate300°C/5.0kgISO 113310.0 cm3/10min
melt mass-flow rate280°C/5.0kgASTM D12383.5 g/10min
Water absorption rate平衡,23°C,50%RHISO 620.060 %
Shrinkage rateMD：--2内部方法0.50-0.70 %
Water absorption rate饱和,23°CISO 620.18 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE JAPAN/V0150B-701
Heat distortion temperature0.45MPa,Unannealed,100mmSpan，HDTISO 75-2/Be140 °C
Linear coefficient of thermal expansionMD：-40到40°CASTME8317.5E-05 cm/cm/°C
vicatASTM D152511155 °C
Heat distortion temperature1.8MPa,Unannealed,100mmSpan，HDTISO 75-2/Ae130 °C
RTI StrUL 746115 °C
vicat--ISO 306/B120155 °C
thermal conductivityISO 83020.27 W/m/K
Linear coefficient of thermal expansionTD：-40到40°CASTME8317.5E-05 cm/cm/°C
vicat--ISO 306/A50160 °C
--ISO 306/B50145 °C
ball-indentation hardness140°C12IEC 60695-10-2Pass
Linear coefficient of thermal expansionMD：23到80°CISO 11359-27E-05 cm/cm/°C
RTI ImpUL 746105 °C
Heat distortion temperature1.8MPa,未退火,3.20mm，HDTASTM D648135 °C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-29E-05 cm/cm/°C
ball-indentation hardness125°CIEC 60695-10-2Pass
RTI ElecUL 746110 °C