PC LNP™ LUBRICOMP™ DFL36-BK 1A665 SABIC INNOVATIVE US

188

Unit Price:US$ 6,880 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Easy to form｜Easy to demould
Application Areas:Electronic and Electrical Applications｜Lighting applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	920 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C3	ISO 180/1U	55 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--1	ASTM D638	9580 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	9080 Mpa
tensile strength	Yield	ASTM D638	123 Mpa
	tensile strength	Yield	ISO 527-2	118 Mpa
		tensile strength	Break	ASTM D638	123 Mpa
		tensile strength	tensile strength	Break	ISO 527-2	118 Mpa
elongation	Yield	ASTM D638	2.6 %
	elongation	Break	ASTM D638	2.8 %
	elongation	elongation	Break	ISO 527-2	2.7 %
Bending modulus	--	ASTM D790	8610 Mpa
Bending modulus	Bending modulus	--	ISO 178	8340 Mpa
bending strength	--	ASTM D790	186 Mpa
bending strength	bending strength	--	ISO 178	185 Mpa
Friction coefficient	Dynamic	ASTM D3702	0.46
Friction coefficient	Friction coefficient	Static	ASTM D3702	0.41
Wear factor		ASTM D3702	4.4E+6 10^-8 mm³/N·m

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			4.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			295 to 305 °C
Temperature in the middle of the barrel			310 to 320 °C
Temperature at the front of the material cylinder			320 to 330 °C
Processing (melt) temperature			305 to 325 °C
Mold temperature			80 to 110 °C
Back pressure			0.200 to 0.300 Mpa
Screw speed			30 to 60 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	143 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	24hr	ASTM D955	0.50 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC LNP™ LUBRICOMP™ DFL36-BK 1A665 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet