Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DFL36-BK 1A665 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Electronic and Electrical Applications,Lighting applications
Easy to form,Easy to demould
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL36-BK 1A665 |
|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 143 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL36-BK 1A665 |
|---|---|---|---|
| Bending modulus | -- | ISO 178 | 8340 Mpa |
| -- | ASTM D790 | 8610 Mpa | |
| bending strength | -- | ASTM D790 | 186 Mpa |
| -- | ISO 178 | 185 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.8 % |
| 断裂 | ISO 527-2 | 2.7 % | |
| 屈服 | ASTM D638 | 2.6 % | |
| Friction coefficient | Static | ASTM D3702 | 0.41 |
| Dynamic | ASTM D3702 | 0.46 | |
| Tensile modulus | --1 | ASTM D638 | 9580 Mpa |
| -- | ISO 527-2/1 | 9080 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 123 Mpa |
| 屈服 | ISO 527-2 | 118 Mpa | |
| 断裂 | ASTM D638 | 123 Mpa | |
| 断裂 | ISO 527-2 | 118 Mpa | |
| Wear factor | ASTM D3702 | 4.4E+6 10^-8 mm³/N·m |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DFL36-BK 1A665 |
|---|---|---|---|
| Shrinkage rate | 24小时 | ASTM D955 | 0.50 % |
| impact performance | Test Condition | Test Method | SABIC INNOVATIVE US/DFL36-BK 1A665 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C3 | ISO 180/1U | 55 kJ/m² |
| 23°C | ASTM D4812 | 920 J/m |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/DFL36-BK 1A665 |
|---|---|---|---|
| Back pressure | 0.200 to 0.300 Mpa | ||
| drying temperature | 120 °C | ||
| drying time | 4.0 hr | ||
| Mold temperature | 80 to 110 °C | ||
| Processing (melt) temperature | 305 to 325 °C | ||
| Screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature at the front of the material cylinder | 320 to 330 °C | ||
| Temperature at the rear of the barrel | 295 to 305 °C | ||
| Temperature in the middle of the barrel | 310 to 320 °C |