Material Description
- Material Properties:UV resistance
- Application Areas:switch|Shell|Roller
- Color:--
- Grade:--
Technical Data Sheet
impact performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Dart impact | 23°C7 | ASTM D3029 | 43.4 J |
23°C | ASTM D3029 | 43.4 J | |
Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
flammability | Test Condition | Test Method | Test Result |
---|---|---|---|
Extreme Oxygen Index | ASTM D2863 | 30 % | |
UL flame retardant rating | 3.0mm | UL 94 | 5VA |
0.64mm | UL 94 | V-0 | |
0.46mm | UL 94 | HB |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
tensile strength | Yield | ASTM D638 | 48.3 Mpa |
Break | ASTM D638 | 48.3 Mpa | |
elongation | Break | ASTM D638 | 110 % |
Bending modulus | 50.0mmSpan | ASTM D790 | 2070 Mpa |
bending strength | Yield,50.0mmSpan | ASTM D790 | 82.7 Mpa |
Break,50.0mmSpan | ASTM D790 | 82.7 Mpa |
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Linear coefficient of thermal expansion | MD:60to138°C | ASTME831 | 1.2E-04 cm/cm/°C |
MD:-40to40°C | ASTME831 | 9.2E-05 cm/cm/°C | |
Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTM D648 | 98.9 °C |
0.45MPa,Unannealed,6.40mm | ASTM D648 | 138 °C | |
RTI | UL 746 | 140 °C | |
RTI Imp | UL 746 | 120 °C | |
RTI Elec | UL 746 | 120 °C |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Outdoor applicability | UL 746C | f2 | |
Water absorption rate | 24hr | ASTM D570 | 0.080 % |
Shrinkage rate | TD4 | Internal Method | 0.90-1.3 % |
TD3 | Internal Method | 1.2-1.6 % | |
MD4 | Internal Method | 0.80-1.1 % | |
MD3 | Internal Method | 1.0-1.4 % | |
Melt Volume Flow Rate (MVR) | 250°C/5.0kg | ISO 1133 | 8.00 cm3/10min |
Specific volume | ASTM D792 | 0.750 cm³/g |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Dielectric constant | 100Hz | ASTM D150 | 3.20 |
1MHz | ASTM D150 | 3.20 | |
Dissipation factor | 100Hz | ASTM D150 | 3E-03 |
1MHz | ASTM D150 | 0.030 | |
Arc resistance | ASTM D495 | PLC6 | |
Dielectric strength | 3.20mm,inOil | ASTM D149 | 19 KV/mm |
3.20mm,inAir | ASTM D149 | 19 KV/mm | |
1.60mm,inOil | ASTM D149 | 25 KV/mm | |
Volume resistivity | ASTM D257 | >1.2E+16 ohms·cm | |
Compared to the anti leakage trace index | CTI | UL 746 | PLC 2 |
High arc combustion index | HAI | UL 746 | PLC 3 |
High voltage arc tracing rate | HVTR | UL 746 | PLC 3 |
Hot wire ignition | HWI | UL 746 | PLC 2 |
hardness | Test Condition | Test Method | Test Result |
---|---|---|---|
Rockwell hardness | R-Scale | ASTM D785 | 117 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.