Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT/PC 357U SABIC INNOVATIVE SHANGHAI
VALOX™
switch、Shell、Roller
UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/357U |
|---|---|---|---|
| Falling hammer impact | 23°C7 | ASTMD3029 | 43.4 J |
| 23°C | ASTMD3029 | 43.4 J | |
| Suspended wall beam without notch impact strength | 23°C | ASTMD4812 | 3200 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/357U |
|---|---|---|---|
| Rockwell hardness | R级 | ASTMD785 | 117 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/357U |
|---|---|---|---|
| Volume resistivity | ASTMD257 | >1.2E+16 ohms·cm | |
| dielectric constant | 1MHz | ASTMD150 | 3.20 |
| Dissipation Factor | 1MHz | ASTMD150 | 0.030 |
| Arc resistance 8 | ASTMD495 | PLC6 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 3 |
| dielectric strength | 3.20mm,inOil | ASTMD149 | 19 KV/mm |
| High arc combustion index (HAI) | HAI | UL746 | PLC 3 |
| dielectric strength | 1.60mm,inOil | ASTMD149 | 25 KV/mm |
| 3.20mm,inAir | ASTMD149 | 19 KV/mm | |
| dielectric constant | 100Hz | ASTMD150 | 3.20 |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 2 |
| Dissipation Factor | 100Hz | ASTMD150 | 3E-03 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 2 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/357U |
|---|---|---|---|
| Bending modulus 6 | 50.0mm跨距 | ASTMD790 | 2070 Mpa |
| Bending strength 6 | 屈服,50.0mm跨距 | ASTMD790 | 82.7 Mpa |
| 断裂,50.0mm跨距 | ASTMD790 | 82.7 Mpa | |
| Tensile strength 5 | 断裂 | ASTMD638 | 48.3 Mpa |
| 屈服 | ASTMD638 | 48.3 Mpa | |
| 断裂 | ASTMD638 | 110 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/357U |
|---|---|---|---|
| Limiting Oxygen Index | ASTMD2863 | 30 % | |
| UL flame retardant rating | 0.64mm | UL94 | V-0 |
| 3.0mm | UL94 | 5VA | |
| 0.46mm | UL94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/357U |
|---|---|---|---|
| Shrinkage rate | TD3 | 内部方法 | 1.2到1.6 % |
| Melt volume flow rate | 250°C/5.0kg | ISO1133 | 8.00 cm3/10min |
| Shrinkage rate | TD4 | 内部方法 | 0.90到1.3 % |
| Water absorption rate | 24hr | ASTMD570 | 0.080 % |
| Specific volume | ASTMD792 | 0.750 cm³/g | |
| Shrinkage rate | MD3 | 内部方法 | 1.0到1.4 % |
| MD4 | 内部方法 | 0.80到1.1 % | |
| Outdoor applicability | UL746C | f2 |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/357U |
|---|---|---|---|
| MD：60到138°C | ASTME831 | 1.2E-04 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 9.2E-05 cm/cm/°C | |
| RTI Elec | UL746 | 120 °C | |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 98.9 °C |
| RTI | UL746 | 140 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 138 °C |
| RTI Imp | UL746 | 120 °C |