PC/PTFE LNP™ LUBRICOMP™ NL001 WH8A511 SABIC INNOVATIVE US

504

Unit Price:US$ 7,780 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
17MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	42.0	J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	13	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	21	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span4	ASTM D790	86.0	Mpa
bending strength	bending strength	--5,6	ISO 178	80.0	Mpa
Bending modulus	--5	ISO 178	2500	Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2440	Mpa
elongation	Break	ISO 527-2/50	20	%
	elongation	Break	ISO 527-2/5	45	%
		elongation	Break3	ASTM D638	24	%
			elongation	Yield	ISO 527-2/5	4.0	%
			elongation	elongation	Yield3	ASTM D638	3.6	%
tensile strength	Break	ISO 527-2/5	40.0	Mpa
	tensile strength	Break3	ASTM D638	43.0	Mpa
		tensile strength	Yield	ISO 527-2/50	50.0	Mpa
			tensile strength	Yield	ISO 527-2/5	45.0	Mpa
			tensile strength	tensile strength	Yield3	ASTM D638	53.0	Mpa
Tensile modulus	--	ISO 527-2/1	2300	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2400	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80	°C
drying time			4.0	hr
Suggested maximum moisture content			0.020	%
Temperature at the rear of the barrel			230 to 245	°C
Temperature in the middle of the barrel			250 to 260	°C
Temperature at the front of the material cylinder			260 to 270	°C
Processing (melt) temperature			250 to 270	°C
Mold temperature			40 to 80	°C
Back pressure			0.200 to 0.300	Mpa
Screw speed			30 to 60	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	95.0	°C
Vicat softening temperature	--	ISO 306/B50	113	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	115	°C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	99.0	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Bf	114	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	116	°C
Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	8.7E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Melt Volume Flow Rate (MVR)	260°C/5.0 kg	ISO 1133	26.0	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	> 1.0E+15	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top