Material Properties:Thermal stability｜Filler: Glass fiber reinforced material｜30% filler by weight
Application Areas:Automotive Applications｜Electronic and electrical components
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.35 g/cm³
Shrinkage rate		ISO 294-4	1.0 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.20 %
Water absorption rate		ISO 62	6.2 %
Water absorption rate	Water absorption rate		ISO 62	1.8 %
MediumDensity			1.31 g/cm³
Ejection Temperature			210 °C
SpecificHeatCapacity of Melt			2200 J/kg/°C
ThermalConductivityofMelt			0.23 W/m/K

flammability	Test Method	Test Result
burning rate	ISO 3795	<100 mm/min
UL flame retardant rating	IEC 60695-11-10,-20	HB
FMVSS flammability	FMVSS302	B

Mechanical properties	Test Method	Test Result
Tensile modulus	ISO 527-2	9500 Mpa
tensile strength	ISO 527-2	160 Mpa
Tensile strain	ISO 527-2	3.3 %

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179/1eA	14 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	210 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	206 °C
vicat		ISO 306/B50	210 °C
melting temperature		ISO 11357-3	220 °C
Linear coefficient of thermal expansion		ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ISO 11359-2	1.2E-04 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.