Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 73G30T BK261 DUPONT USA
Zytel®
Automotive Applications、Electronic and electrical
Thermal stability、Filler: Glass fiber reinf、30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/73G30T BK261 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 kJ/m² |
| -30°C | ISO 179/1eA | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/73G30T BK261 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.3 % |
| tensile strength | 断裂 | ISO 527-2 | 160 Mpa |
| flammability | Test Condition | Test Method | DUPONT USA/73G30T BK261 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | FMVSS302 | B | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| physical property | Test Condition | Test Method | DUPONT USA/73G30T BK261 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.0 % |
| MD | ISO 294-4 | 0.20 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 6.2 % |
| MediumDensity | 1.31 g/cm³ | ||
| Ejection Temperature | 210 °C | ||
| density | ISO 1183 | 1.35 g/cm³ | |
| SpecificHeatCapacity of Melt | 2200 J/kg/°C | ||
| ThermalConductivityofMelt | 0.23 W/m/K | ||
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.8 % |
| Thermal performance | Test Condition | Test Method | DUPONT USA/73G30T BK261 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 220 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C |
| Linear coefficient of thermal expansion | TD2 | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| vicat | ISO 306/B50 | 210 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 206 °C |
| Linear coefficient of thermal expansion | MD2 | ISO 11359-2 | 3E-05 cm/cm/°C |