SPS XAREC™ SP151 IDEMITSU JAPAN

514

Unit Price:US$ 3,100 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
25MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced｜High temperature resistance｜Injection grade
Application Areas:Electrical applications｜Household daily necessities
Color:--
Grade:Electroplating grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180	29	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	32	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D790/ISO 178	165	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	9.8	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	47
tensile strength		ASTM D638/ISO 527	100	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	2.1	%
Tensile modulus		ISO 527-2	11000	Mpa
tensile strength	Break	ISO 527-2	100	Mpa
Tensile strain	Break	ISO 527-2	2.1	%
Bending modulus		ISO 178	9800	Mpa
bending strength		ISO 178	165	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：-30to30°C	TMA	4.9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-30to30°C	TMA	2.2E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	230	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	265	°C
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	MD 2.2	mm/mm.℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD	Internal Method	0.30-0.70	%
Water absorption rate		ASTM D570/ISO 62	0.02	%
Shrinkage rate		ASTM D955	MD 0.1-0.4	%
density		ASTM D792/ISO 1183	1.41
Shrinkage rate	MD	Internal Method	0.10-0.40	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.020	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	1MHz	IEC 60250	3.40
Dielectric strength		ASTM D149	50	KV/mm
Volume resistivity		IEC 60093	>1.0E+16	ohms·cm
Compared to the anti leakage trace index	CTI)3	IEC 60112	PLC 0
Arc resistance		ASTM D495	PLC6
Dissipation factor	1MHz	IEC 60250	<1.0E-3
Volume resistivity		ASTM D257/IEC 60093	>1.0*10^16	Ω.cm
Arc resistance		ASTM D495/IEC 60112	110

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

SPS XAREC™ SP151 IDEMITSU JAPAN

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index